Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 8.23 GPa | 1190 ksi | ASTM D 790 |
SABIC Innovative Plastics Valox® AB9530 ABS+PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Modulus | 8.23 GPa | 1190 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF006LXN PC LNP* THERMOCOMP* DF006LXN is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material are: Low Extractable, NSF Listed. |
|||
Flexural Modulus | 8.23 GPa | 1190 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP DF006 PC LNP* Thermocomp* DF006 is a compound based on Polycarbonate resin containing 30% Glass Fiber. |
|||
Flexural Modulus | 8.23 GPa | 1190 ksi | ASTM D790 |
SABIC Innovative Plastics NORYL CN5246 PPE+PS (Asia Pacific) |