Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 4.83 GPa | 701 ksi | ASTM D790 |
PolyOne Edgetek® NY-20GF/10GB/000 Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
Flexural Modulus | 4.83 GPa | 701 ksi | ASTM D790 |
PolyOne Edgetek® NY-20GF/10GB/000 Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
Flexural Modulus | 4.83 GPa | 701 ksi | ASTM Data |
BASF Capron® HPN 9315G HS BK-102 Impact Modified, 15% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9315G HS BK-102 is a 15% glass reinforced impact modified, heat stabilized, pigmented black, nylon 6 injection molding grade resin. It is in the High Productivity Nylon Series developed .. |
|||
Flexural Modulus | 4.83 - 12.4795 GPa @Temperature -40.0 - 121 °C |
701 - 1810.03 ksi @Temperature -40.0 - 250 °F |
Average value: 6.81 GPa Grade Count:5 |
Overview of materials for Nylon 6, 40% Glass Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, 40% Glass Fiber Filled". Specific grades with glass content between 35% and 44% are included. E.. |
|||
Flexural Modulus | 4.83 GPa | 701 ksi | Method I (3 point load), 2.0 mm/min; ASTM D790 |
Styron CALIBREâ„¢ 5201-12 Polycarbonate Resin Overview: CALIBREâ„¢ 5201-12 polycarbonate resin is 20% glass reinforced containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. CALI.. |
|||
Flexural Modulus | 4.83 GPa | 701 ksi | Method I (3 point load), 2.0 mm/min; ASTM D790 |
Styron CALIBREâ„¢ 5201-8 Polycarbonate Resin Overview: CALIBREâ„¢ 5201-8 polycarbonate resin is 20% glass reinforced containing mold release for optimal processing. This resin exhibits high modulus and excellent dimensional stability. CALIB.. |
|||
Flexural Modulus | 4.83 GPa | 701 ksi | ASTM D790 |
Chesterton ARC MXHT High temperature severe wear compound Description: An advanced ceramic composite for the protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack at elevated temperatures. It is applied at a thickness o.. |
|||
Flexural Modulus | 4.83 GPa | 701 ksi | ASTM D790 |
Chesterton ARC MXC Castable Extreme Wear Compound Description: An advanced ceramic composite, with flowable viscosity, for the repair and protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack. It can be hand tro.. |
|||
Flexural Modulus | 4.83 GPa | 701 ksi | ASTM Test |
BASF Ultradur B 4300 G3 15% Glass Filled PBT Ultradur B 4300 G3 is an easy flowing injection molding PBT with 15% glass fiber reinforcement for rigid, tough, and dimensionally stable parts. |
|||
Flexural Modulus | 4.83 GPa @Temperature 120 °C |
701 ksi @Temperature 248 °F |
ASTM Test |
BASF Ultramid® 8234G HS 44% Glass Filled PA6 (Dry) Ultramid 8234G HS is a heat stabilized, 44% glass fiber reinforced polyamide 6 injection molding compound offering the highest level of strength, stiffness, high temperature performance and dimensio.. |
|||
Flexural Modulus | 4.83 GPa | 701 ksi | ASTM Test |
BASF Ultramid® 8333G HI 33% Glass Filled PA6 (Conditioned) Ultramid 8333G HI is a 14% glass reinforced, impact modified PA6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a
balance of st.. |
|||
Flexural Modulus | 4.83 GPa | 701 ksi | ASTM Data |
BASF Capron® 8333G HI Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)
(discontinued **) Capron 8333G HI is a 33% glass reinforced, impact modified polyamide 6 injection molding compound developed for applications requiring improved dry as molded toughness in combination with a balance .. |
|||
Flexural Modulus | 4.83 GPa | 701 ksi | ASTM Data |
BASF Capron® HPN 9315G Impact Modified, 15% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron HPN 9315G is a 15% glass reinforced, impact modified polyamide 6 injection molding grade resin in the High Productivity Nylon Series developed for applications requiring superior dry-as-molde.. |