Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 7.86 GPa | 1140 ksi | |
Plastcom SLOVAMID 6 GF 30 FRG 4 LW PA6, 30% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 30% glass fibre, with nonhalogen flame retardant. Main features: flammability in accordance with UL 94 V0 at 1.6 mm, glow wire at 960°.. |
|||
Flexural Modulus | 7.86 GPa | 1140 ksi | ASTM D790 |
Solvay Specialty Polymers Amodel® AT-6130 HS Polyphthalamide (PPA), 30% Glass Fiber (Dry) Amodel® AT-6130 HS is a 30% glass-reinforced, toughened polyphthalamide (PPA) resin that has more elongation than other 30% glass-reinforced grades of Amodel® resin. This grade was developed f.. |
|||
Flexural Modulus | 7.86 GPa | 1140 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP DF006LXN PC LNP* THERMOCOMP* DF006LXN is a compound based on Polycarbonate resin containing 30% Glass Fiber. Added features of this material are: Low Extractable, NSF Listed. |
|||
Flexural Modulus | 7.86 GPa | 1140 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP QF006 PA 6/10 LNP THERMOCOMP* QF006 is a compound based on Nylon 6/10 resin containing 30% Glass Fiber. |
|||
Flexural Modulus | 7.86 GPa | 1140 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL GTX RNX130 PPE+PS+PA 30% glass reinforced PPE+PS+PA alloy for automotive and nonautomotive applications. Recycle grade in black/gray only. |
|||
Flexural Modulus | 7.86 GPa | 1140 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP DF006 PC LNP* Thermocomp* DF006 is a compound based on Polycarbonate resin containing 30% Glass Fiber. |
|||
Flexural Modulus | 7.86 GPa | 1140 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF VX00585 PA 66 LNP* Thermotuf* VX00585 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
Flexural Modulus | 7.86 GPa | 1140 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF VX00585 PA 66 (Asia Pacific) LNP* Thermotuf* VX00585 is a compound based on Nylon 66 resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
Flexural Modulus | 7.86 GPa | 1140 ksi | ASTM D790 |
PlastxWorld CEVIAN® SERG3 30% GF ABS Glass fiber reinforced and flame retarded ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by PlastxWorld Inc. |
|||
Flexural Modulus | 7.86 GPa | 1140 ksi | ASTM D790 |
PlastxWorld CEVIAN® SKG30 30% GF ABS Glass fiber reinforced, heat resistant and flame retarded ABS.These are typical values and are not intended for specification purposes. UL approved file No. is E47773. Information provided by Plast.. |
|||
Flexural Modulus | 7.86 GPa | 1140 ksi | ASTM Data |
BASF Capron® 8333G Impact Modified, 33% Glass-Filled Nylon 6 (Dry)
(discontinued **) Capron 8333G is a 33% glass reinforced nylon 6 modified compound developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness, and excel.. |
|||
Flexural Modulus | 7.86 GPa | 1140 ksi | ASTM D790 |
LNP Thermocomp® QF-1006 Polyamide 6/10 Copolymer, Glass Fiber Reinforcement
(discontinued **) Forms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades are still active under new names.. |
|||
Flexural Modulus | 7.86 GPa | 1140 ksi | ASTM D790 |
Solvay Specialty Polymers Amodel® AT-6130 HS Polyphthalamide (PPA)
(Unverified Data**) Amodel AT-6130 HS is a 30% glass-reinforced, toughened polyphthalamide (PPA) resin that has more elongation than other 30% glass-reinforced grades of Amodel resin. This grade was developed for autom.. |