Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 7.03 GPa | 1020 ksi | ASTM D790 |
SABIC Innovative Plastics LNP STAT-KON AE002 ABS (Asia Pacific) LNP* Stat-kon* AE002 is a compound based on Acrylonitrile Butadiene Styrene resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. |
|||
Flexural Modulus | 7.03 GPa | 1020 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP 9X02540 PC+PET LNP* THERMOCOMP* PDX-02540 is a compound based on a PET+PC Blend containing Proprietary Filler. Flame Retardant. |
|||
Flexural Modulus | 7.03 GPa | 1020 ksi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp OF003A PPS LNP* Thermocomp* OF003A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber.This data was supplied by SABIC-IP for the Americas region. |
|||
Flexural Modulus | 7.03 GPa | 1020 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF QX01581H PA6.10 LNP THERMOTUF* QX01581H is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
Flexural Modulus | 7.03 GPa | 1020 ksi | ASTM D 790 |
SABIC Innovative Plastics LNP Thermocomp OF003A PPS (Asia Pacific) LNP* Thermocomp* OF003A is a compound based on Polyphenylene Sulfide resin containing Glass Fiber.This data was supplied by SABIC-IP for the Asia Pacific region. |
|||
Flexural Modulus | 7.03 GPa | 1020 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOTUF QX01581H PA 6/10 (Asia Pacific) LNP* THERMOTUF* QX01581H is a compound based on Nylon 6/10 resin containing Glass Fiber. Added features of this material include: High Impact. |
|||
Flexural Modulus | 7.03 GPa | 1020 ksi | ASTM D790 |
LNP Thermotuf® QF-1006 HI Polyamide 6/10 Copolymer, Glass Fiber Reinforcement
(discontinued **) Features: High Impact ResistanceForms: PelletsProcessing Method: Injection MoldingInformation provided by LNP, a GE Plastics Company.This data sheet is labeled Discontinued; however many LNP grades .. |