Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 4.39 GPa | 637 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP WAL34 PBT LNP* LUBRICOMP* WAL34 is a compound based on (PBT resin containing 15% PTFE, 20% Aramid Fiber. Added features of this material include: Wesr Resistant. |
|||
Flexural Modulus | 4.39 GPa | 637 ksi | ASTM D790 |
SABIC Innovative Plastics LNP LUBRICOMP WAL34 PBT (Asia Pacific) LNP* Lubricomp* WAL34 is a compound based on Polybutylene Terephalate resin containing PTFE, Aramid Fiber. Added features of this material include: Internally Lubricated. |
|||
Flexural Modulus | 4.39 GPa | 637 ksi | ASTM D790 |
SABIC Innovative Plastics LNP THERMOCOMP WX05456 Polyester, TP LNP THERMOCOMP* WX05456 is a compound based on Polyester, TP resin containing Mineral. |
|||
Flexural Modulus | 4.39 GPa | 637 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP THERMOCOMP ZX06323 PPE+HIPS (Asia Pacific) This material is mineral filled PPO grade with high dielectric constant and low loss tangent |
|||
Flexural Modulus | 4.39 GPa | 637 ksi | ISO 178 |
BASF Ultramid® TG3S 15% Glass Filled PA6 (Dry) Description: Ultramid TG3S is a 15% glass reinforced, heat stabilized, impact modified PA6 injection molding compound developed for applications requiring improved toughness in combination with a ba.. |
|||
Flexural Modulus | 4.39 GPa | 637 ksi | ISO Data |
BASF Ultramid® TG3S BK-104 15% Glass Filled PA6 (Dry) Ultramid TG3S BK-104 is a 15% glass reinforced, heat stabilized, impact modified PA6 injection molding compound developed for applications requiring improved toughness in combination with a balance .. |