Polymer Property : Flexural Modulus = 611 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	4.21 GPa	611 ksi	Tangent; ASTM D790
Multibase Nylex™ 2185 R30 Polyamide + PP Glass fiber reinforcement, 30% Filler by Weight Features: Crack Resistance, GoodDimensional Stability, GoodImpact Resistance, GoodMoisture ResistantProcessability, GoodForms:PelletsProcessing Method..
Flexural Modulus	4.21 GPa @Temperature 175 °C	611 ksi @Temperature 347 °F	ISO 178
Solvay Specialty Polymers Amodel® AS-4133 HS Polyphthalamide (PPA) (Unverified Data**) Amodel AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Typical applications include ..
Flexural Modulus	4.21 GPa	611 ksi	2 mm/min; ISO 178
SABIC Innovative Plastics REMEX VR4831 PBT 15% Glass filled PBT, Flame retardant, UL Recognized, Utility grade, Black color only
Flexural Modulus	4.21 GPa	611 ksi	1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics SABIC PPCOMPOUND G3220A PP SABICÂ® PPcompound G3220A is a general purpose, 20% glass filled, chemically coupled, heat stabilized homopolymer polypropylene compound. The IMDS is 209767996.
Flexural Modulus	4.21 GPa @Temperature 175 Â°C	611 ksi @Temperature 347 Â°F	ISO 178
Solvay Specialty Polymers AmodelÂ® AS-4133 HS Polyphthalamide (PPA), 33% Glass Fiber (Dry) AmodelÂ® AS-4133 HS is a 33% glass reinforced, lubricated, heat stabilized grade of polyphthalamide (PPA) that offers fast cycle times and moldability in hot water molds. Testing conducted on samp..
Flexural Modulus	4.21 GPa	611 ksi	ASTM D 790
SABIC Innovative Plastics ValoxÂ® TS4016 PBT (Asia Pacific) This data was supplied by SABIC-IP for the Asia Pacific region.
Flexural Modulus	4.21 GPa @Temperature 175 °C	611 ksi @Temperature 347 °F	ISO 178
Solvay Specialty Polymers Amodel® AS-4133 HN Polyphthalamide (PPA), Dry, 33% Glass Fiber Reinforcement, Heat Stabilizer Amodel AS-4133 HN polyphthalamide (PPA) is a non-lubricated, heat stabilized grade that offers fast cycle times and is hot-water moldable. Typical applications include electrical and electronic comp..
Flexural Modulus	4.21 GPa	611 ksi	1.3 mm/min, 50 mm span; ASTM D 790
SABIC Innovative Plastics LNP Thermocomp FF006 PE LNP Thermocomp FF-1006 is a glass filled Polyethylene.This data was supplied by SABIC-IP for the Americas region.