Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 4.55 GPa | 660 ksi | |
Plastcom SLOVALEN PH 69 GF 20 T 10 PP, 20% glass fibre FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 20% glass fibre and 10 % Talc, contains themodifier of mechanical properties.Increased strength in comparison with .. |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | 1.3 mm/min; ASTM D790 |
PolyOne Gravi-Tech™ GT6000-0023 Black Polyamide 6 (Nylon 6) Information provided by PolyOne |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | |
Plastcom SLOVAMID 6 GF 7 T 13 PA6, 7% glass fibre, 13% mineral filling FeaturesGood anisotropy of the manufacturing shrinkage. The talc is added to get the material shrinkage identical in both directions. Application for flat products in disc form /no screw after cooli.. |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | |
Plastcom SLOVAMID 66 GB 30 LS PA66, 30% glass beads, light stability Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.0.. |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS High heat PC/ABS blend offering high modulus / low CTE and good practical impact |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS (Asia Pacific) High heat PC/ABS blend offering high modulus / low CTE and good practical impact |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
SABIC Innovative Plastics Cycoloy® XCM851 PC+ABS (Europe-Africa-Middle East) High heat PC/ABS blend offering high modulus / low CTE and good practical impactThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region. |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | ASTM D790 |
PolyOne Edgetek® XT XT-115GF-AX00 PC+PBT with Glass Fiber Reinforcement
(discontinued **) EDGETEK™ XT High Performance Polymers are polycarbonate and polyester alloys that combine strength, durability and chemical resistance. The Edgetek XT product family includes a complete line of gen.. |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | ASTM D790 |
PolyOne Edgetek® XT XT-115GF-AX01-HF PC+PBT with Glass Fiber Reinforcement
(discontinued **) EDGETEK™ XT High Performance Polymers are polycarbonate and polyester alloys that combine strength, durability and chemical resistance. The Edgetek XT product family includes a complete line of gen.. |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | ASTM D790 |
LyondellBasell Hostacomâ„¢ BJ23A Polypropylene Copolymer Description: Hostacomâ„¢ BJ23A is a polypropylene copolymer that is used for appliance componentsFeatures: Good StiffnessGood FlowChemically CoupledGood Impact ResistanceInformation provided by B.. |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | ASTM D790 |
Techmer ES Luriblend® PC GF30 TS15 BK 30% Glass Filled Availability: North AmericaForms: PelletsFiller/Reinforcement: Glass Fiber, 30% Filler by WeightAdditive: PTFE + Silicone LubricantFeatures: LubricatedAppearance: BlackInformation provided by TP Com.. |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL EM7304F PPE+PS 15% glass reinforced, high flow with enhanced polyurethane foam adhesion for instrument panel retainers. |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | ISO 178 |
Borealis Nepol™ GB601HP Polypropylene, 20% Long Glass Fiber Reinforced w/BJ356MO Nepol™ GB601HP is a special long glass fiber reinforced polypropylene concentrate grade intended for injection molding and extrusion. This material is designed for the dilution process in combinat.. |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | ASTM D790 |
Asahi Kasei Thermylene® P6-25FG-0687 25% Glass Fiber Reinforced Information provided by Asahi Thermofil |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | XY direction; ASTM D790 |
ALM PA 620-MF Mineral Fiber Filled Nylon 12 SLS Prototyping Polymer Information provided by Advanced Laser Materials (ALM). |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | ASTM D790 |
Asahi Kasei Thermofil P6-30FM-0801 30% Fiber Mineral Filled, Heat Stabilized Information provided by Asahi Thermofil |
|||
Flexural Modulus | 4.55 GPa | 660 ksi | ASTM D790 |
Aaron Industries AAROPRENE® GFIPP 2030 High Impact Glass Filled Polypropylene AAROPRENE® GFIPP 2000 Series Reinforced CompoundsMelt flow index may be specified. Color may be specified. |