- Polymer Property : Flexural Modulus = 4.51 GPa
Polymer Property : Flexural Modulus = 4.51 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 4.51 GPa | 654 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Cycoloy® CM6240 PC+ABS (Asia Pacific) CYCOLOY CM6240 resin is a flame retardant PC/ABS blend featuring balanced properties of high modulus, good flow and ductility. It is of Br- & Cl-free flame retardant systems intended to meet thin wa.. |
|||
| Flexural Modulus | 4.51 GPa @Thickness 3.20 mm |
654 ksi @Thickness 0.126 in |
1.3mm/min; ASTM D790 |
| LG Chemical LUPOY SC2202 PC+GF20%, High Impact Description: Injection Molding, PC+GF20%, Good Toughness, Good Impact, Chemical ResistanceApplication: Mobile Phone HousingCAS: 103598-77-2 and 65997-17-3Information provided by LG Chemical |
|||
| Flexural Modulus | 4.51 GPa | 654 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP THERMOCOMP AF003 ABS LNP* THERMOCOMP* AF003 is a compound based on ABS resin containing 15% Glass Fiber. |
|||
| Flexural Modulus | 4.51 GPa | 654 ksi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Infino® LS-1150G PC/ABS, 15% Glass Filled FR 15% GF reinforcement; can be used in mold frames for LCD BLU.Information provided by Samsung Cheil Industries. |
|||
| Flexural Modulus | 4.51 GPa | 654 ksi | 2.8 mm/min; ASTM D790 |
| Samsung Cheil Industries Infino® LS-1150G PC/ABS, 15% Glass Filled FR 15% GF reinforcement; can be used in mold frames for LCD BLU.Information provided by Samsung Cheil Industries. |
|||
| Flexural Modulus | 4.51 GPa | 654 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP RF003H PA 66 LNP* THERMOCOMP* RF003H is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
| Flexural Modulus | 4.51 GPa | 654 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP RF003XXH PA 66 LNP* THERMOCOMP* RF003XXH is a compound based on Nylon 66 containing 15% Glass Fiber. Added feature of this grade is: Healthcare. |
|||
| Flexural Modulus | 4.51 GPa @Thickness 6.40 mm |
654 ksi @Thickness 0.252 in |
ASTM D-790 |
| Bhansali Engineering Abstron IMG1130 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali |
|||
| Flexural Modulus | 4.51 GPa @Thickness 6.40 mm |
654 ksi @Thickness 0.252 in |
ASTM D-790 |
| Bhansali Engineering Abstron IMG1130 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali |
|||
| Flexural Modulus | 4.51 GPa | 654 ksi | ASTM D790 |
| SABIC Innovative Plastics Lexan® ML3260 PC (Asia Pacific) |
|||
| Flexural Modulus | 4.51 GPa @Thickness 6.40 mm |
654 ksi @Thickness 0.252 in |
ASTM D-790 |
| Bhansali Engineering Abstron IMGS20 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali |
|||
| Flexural Modulus | 4.51 GPa @Thickness 6.40 mm |
654 ksi @Thickness 0.252 in |
ASTM D-790 |
| Bhansali Engineering Abstron IMGS20 Glass Reinforced Grade Glass Reinforced ABS & SAN Resins for product specific requirement of very high rigidity and temperatureInformation provided by Bhansali |
|||