Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 2.15 - 2.40 GPa | 312 - 348 ksi | ASTM D790 |
Prodways PLASTCure Model 300 3D Printing Polymer Good mechanical properties.Broad range of dental model applications.Information provided by Genistar. |
|||
Flexural Modulus | 2.10 - 2.40 GPa | 305 - 348 ksi | ASTM D790-04 |
Proto3000 Objet Digital Materials™ DM_7230 Transparent Prototyping Polymer Primary material: FullCure720Secondary material: TangoBlackDigital Materials are made up of two Objet materials. The two materials are combined in specific concentrations and structures, to provide .. |
|||
Flexural Modulus | 2.30 - 2.40 GPa @Temperature -20.0 - -20.0 °C |
334 - 348 ksi @Temperature -4.00 - -4.00 °F |
Average value: 2.32 GPa Grade Count:5 |
Overview of materials for Polypropylene with 20% Talc Filler This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Talc Filler".Specific grades with primary filler content between 15% and 24% are .. |
|||
Flexural Modulus | 2.00 - 2.40 GPa | 290 - 348 ksi | ASTM D790 |
Huntsman RenShape® SL 7820 Stereolithography Plastic RenShape® SL 7820 stereolithography material is a white, low viscosity and stable liquid that produces strong black models and prototypes with good surface fi nish and detail, and ABS-like appear.. |
|||
Flexural Modulus | 2.20 - 2.40 GPa | 319 - 348 ksi | ASTM D790 |
Loxim 600 00HB Polycarbonate/Polybutylene Terephthalate Information provided by Loxim Industries |
|||
Flexural Modulus | 2.20 - 2.40 GPa | 319 - 348 ksi | ASTM D790 |
Loxim 831 02T HB Polypropylene Compound, 30% Talc Filled, Flame Retardant Information provided by Loxim Industries |