- Polymer Property : Flexural Modulus = 2.03 GPa
Polymer Property : Flexural Modulus = 2.03 GPa Product List
Mechanical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Modulus | 2.03 GPa | 295 ksi | ASTM D790 |
| Omni Plastics OmniTuff™ CPP CCF40 Copolymer Polypropylene Calcium Carbonate Filled Applications: Structural parts across industry segments including pump housings, wheels, handles, mountings, brackets, levers, pressure vessels, and furniture components.Information provided by Omni.. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® EM1210 PC Automotive interiors. Excellent heat/impact resistance and outstanding property retention over wide temperature range/severe automotive conditions |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® EM1210 PC (Asia Pacific) Automotive interiors. Excellent heat/impact resistance and outstanding property retention over wide temperature range/severe automotive conditions |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® EM3110 PC Automotive interiors. Optimizes flow/processability for cost effective thinner wall design uses. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Lexan® EM3110 PC (Asia Pacific) Automotive interiors. Optimizes flow/processability for cost effective thinner wall design uses. |
|||
| Flexural Modulus | 2.03 GPa | 295 ksi | ASTM D790 |
| Polymer Resources PC-IM3 Polycarbonate, Impact Modified, High Flow Polycarbonate, Impact Modified, High FlowProcess: Injection MoldingNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by.. |
|||
| Flexural Modulus | 2.03 GPa | 295 ksi | Tangent; ASTM D790 |
| RheTech Products HP511-00 27% Talc Reinforced Polypropylene Copolymer, High Performance, Non-UV Stabilized, Natural Applications: Interior trimCenter consolesI/P componentsInjection molding conditions reported in table.Information provided by RheTech Products. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics Cycolac® BDT5510 ABS Automotive. High heat resistance, low gloss, color concentratable for interior applications. Natural only. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | ASTM D790 |
| SABIC Innovative Plastics Lexan® SLD3000 PC (Asia Pacific) Antistatic colorable/opaque FR PC grade |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 80x10x4 mm specimen, 2 mm/min; ISO 178 |
| LyondellBasell SEQUEL® 1825 Engineered Polyolefin Description: SEQUEL® 1825 engineered polyolefin is designed for automotive applications that require energy management combined with ductility and a balance of stiffness and impact resistance ove.. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | |
| Kraton® FG1901 + PA-6,6 blend (20/80) Blending KRATON D and G polymers with PA significantly improves the toughness at both room and low temperatures. KRATON polymers are block segments of styrene and rubber monomers (A-B, A-B-A, or [A.. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | ISO 178 |
| Ineos ABS Lustran® SMA 2171 SMA, Injection Molding Grade Lustran® SMA 2171 is a high heat injection molding grade of impact-modified SMA (styrene/maleic anhydride) terpolymer offering an exceptional balance of processability and performance. Lustran®.. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP LUBRICOMP DP001E PC LNP* LUBRICOMP* DP001E is a Polycarbonate base resin containing 5% PTFE/Silicone. Added features are: Internally Lubricated, Easy Molding. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR5210R PC (Asia Pacific) Wear resistant, 7% PTFE filled PC. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics PREVEX W20 PPE+PS (Asia Pacific) Automotive. PPE alloy. High flow/impact. Instrument panels and interior trim components. HDT 210F. |
|||
| Flexural Modulus | 2.03 GPa | 295 ksi | ASTM D790 |
| Techmer ES Elastoblend® PA12 CL Availability: North AmericaForms: PelletsAppearance: Clear/TransparentInformation provided by TP Composites, Inc. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics LNP STAT-KON AX01706 ABS LNP* STAT-KON* AX01706 is a compound based on ABS containing proprietary fillers. Added feature of this grade is: Electrically Conductive. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Xenoy® 5220U PBT+PC Unreinforced PBT+PC Alloy. Impact Modified. Improved retention of mechanical properties under UV exposure. Excellent low temperature impact and chemical resistance. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics Xenoy® 5220U PBT+PC (Asia Pacific) Unreinforced PBT+PC Alloy. Impact Modified. Improved retention of mechanical properties under UV exposure. Excellent low temperature impact and chemical resistance. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| SABIC Innovative Plastics LNP STAT-KON WS002I PBT LNP* STAT-KON* WS002I is a compound based on PBT resin containing 10% Stainless Steel. Added features of this material include: Electrically Conductive, High Impact. |
|||
| Flexural Modulus | 2.03 GPa | 295 ksi | ASTM D790 |
| Star Plastics PC/PBT7820 Molding Grade PC/PBT Information provided by Star Plastics, Inc. |
|||
| Flexural Modulus | 2.03 GPa | 295 ksi | ASTM D790 |
| Techmer ES Plastiblend® ABS 8003 A1 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer and Impact ModifierFeatures: Heat Stabilized and Impact ModifiedProcessing Method: Injection MoldingInformation provided by TP Comp.. |
|||
| Flexural Modulus | 2.03 GPa | 295 ksi | ASTM D790 |
| Techmer ES Plastiblend® PA6/6 HS L N Nylon 66 Availability: North AmericaForms: PelletsAdditive: Heat Stabilizer, Impact Modifier and Nucleating AgentFeatures: Heat Stabilized, Impact Modified and NucleatedProcessing Method: Injection MoldingIn.. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics XYLEX X7519HP PC+POLYESTER Good Chemical Resistance, XYLEX grade with good dishwasher performance, USA/Europe Food Contact Comment: While molding of thicker parts, cooling speed has an influence of transparency. Thicker parts.. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics XYLEX X7519HP PC+POLYESTER (Asia Pacific) Good Chemical Resistance, XYLEX grade with good dishwasher performance, USA/Europe Food Contact Comment: While molding of thicker parts, cooling speed has an influence of transparency. Thicker parts.. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | ASTM D790 |
| SABIC Innovative Plastics LNP THERMOCOMP WX02869H Polyester, TP LNP THERMOCOMP* WX02869H is a compound based on Polyester, TP resin containing High Specific Gravity. Added features of this material include: High Impact. |
|||
| Flexural Modulus | 2.03 GPa | 295 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Diamond Polymers ABS 7600B Description: Blow Molding Grade, Extra High ImpactInformation provided by Diamond Polymers, Inc. |
|||
| Flexural Modulus | 2.03 GPa | 295 ksi | ASTM D790 |
| Amco Amalloy® B9674 Polymer Alloy Amco Amalloy B9674 is a clear performance copolymer with exceptional clarity and toughness.Good melt flow, and impact strength.Information provided by Amco Plastic Materials. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 2 mm/min; ISO 178 |
| SABIC Innovative Plastics XYLEX X7519HP PC+POLYESTER (Europe-Africa-Middle East) Good Chemical Resistance, XYLEX grade with good dishwasher performance, USA/Europe Food Contact Comment: While molding of thicker parts, cooling speed has an influence of transparency. Thicker parts.. |
|||
| Flexural Modulus | 2.03 GPa | 294 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| SABIC Innovative Plastics PREVEX W20 PPE+PS Automotive. PPE alloy. High flow/impact. Instrument panels and interior trim components. HDT 210F. |
|||