Polymer Property : Flexural Modulus = 177 ksi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Modulus 1.22 GPa

@Temperature 23.0 °C
177 ksi

@Temperature 73.4 °F
ASTM D790A
Ineos H36G-01 Polypropylene Homopolymer
This is a polypropylene homopolymer for general purpose injection molding and high speed fiber spinning applications. It is useful for spunbonded nonwovens and partially oriented yarn (POY). This ..
Flexural Modulus 1.22 GPa
177 ksi
2% secant; ASTM D790-02
Ipiranga Petrochem GD 5160 HDPE
IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce ..
Flexural Modulus 1.22 GPa
177 ksi
1% secant; ASTM D790-02
Ipiranga Petrochem PRA 0852 Polypropylene
The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr..
Flexural Modulus 1.22 GPa
177 ksi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP THERMOTUF VX99809 Super Tough Nylon
Super Tough Nylon, Proprietary Filler(s),
Flexural Modulus 1.22 GPa
177 ksi
at 1% secant modulus; ASTM D790
A. Schulman POLYAXIS® PD8020 Polypropylene
DescriptionPolyaxis PD 8020 is a polypropylene designed from rotational molding with a combination of good stiffness and ESCR.NOTE: Physical properties are based on rotationally molded samples from ..
Flexural Modulus 1.22 GPa
177 ksi
ASTM D790
UBE UBESTA® 3020X25L Rigid Automotive Grade Nylon 12
Description: UBE UBESTA® Automotive grade Nylon 12Comments: for coating steel and aluminumInformation provided by UBE.
Flexural Modulus 1.22 GPa
177 ksi
at 1% secant modulus; ASTM D790
A. Schulman POLYAXIS® PD8020 Polypropylene
DescriptionPolyaxis PD 8020 is a polypropylene designed from rotational molding with a combination of good stiffness and ESCR.NOTE: Physical properties are based on rotationally molded samples from ..
Flexural Modulus 1.22 GPa
177 ksi
at 1% secant modulus; ASTM D790
A. Schulman POLYAXIS® PD8020 Polypropylene
DescriptionPolyaxis PD 8020 is a polypropylene designed from rotational molding with a combination of good stiffness and ESCR.NOTE: Physical properties are based on rotationally molded samples from ..
Flexural Modulus 1.22 GPa
177 ksi
at 1% secant modulus; ASTM D790
A. Schulman POLYAXIS® PD8020 Polypropylene
DescriptionPolyaxis PD 8020 is a polypropylene designed from rotational molding with a combination of good stiffness and ESCR.NOTE: Physical properties are based on rotationally molded samples from ..
Flexural Modulus 1.22 GPa
177 ksi
at 1% secant modulus; ASTM D790
A. Schulman POLYAXIS® PD8020 Polypropylene
DescriptionPolyaxis PD 8020 is a polypropylene designed from rotational molding with a combination of good stiffness and ESCR.NOTE: Physical properties are based on rotationally molded samples from ..
Flexural Modulus 1.22 GPa
177 ksi
at 1% secant modulus; ASTM D790
A. Schulman POLYAXIS® PD8020 Polypropylene
DescriptionPolyaxis PD 8020 is a polypropylene designed from rotational molding with a combination of good stiffness and ESCR.NOTE: Physical properties are based on rotationally molded samples from ..
Flexural Modulus 1.22 GPa
177 ksi
ASTM D790
NOVA Chemicals Novapol® HB-L455-A HDPE Blow Molding Resin  (discontinued **)
Molded Plaque Properties. Features: excellent processability on high speed, multiple-head blow molding lines, good balance of physical and molding properties.Applications: chemical bottles, toys.Da..