Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 5.17 - 10.3 GPa | 750 - 1500 ksi | Average value: 8.71 GPa Grade Count:19 |
Overview of materials for Polyetherimide (PEI), 30% Glass Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 30% Glass Fiber". Specific grades with glass content between 25% and 34% are included. E.. |
|||
Flexural Modulus | 1.31 - 10.3 GPa | 190 - 1500 ksi | Average value: 4.09 GPa Grade Count:21 |
Overview of materials for Polyphenylene Sulfide (PPS) with PTFE Filler This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with PTFE Filler". Each property range of values reported is minimum and max.. |
|||
Flexural Modulus | 2.48 - 10.3 GPa | 360 - 1500 ksi | Average value: 4.62 GPa Grade Count:97 |
Overview of materials for Nylon 66, Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Bead Filled". Each property range of values reported is minimum and maximum values of ap.. |
|||
Flexural Modulus | 1.80 - 10.3 GPa | 261 - 1500 ksi | Average value: 6.16 GPa Grade Count:86 |
Overview of materials for Nylon 66, 40% Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, 40% Mineral Filled". Specific grades with primary filler content between 35% and 44% are inclu.. |
|||
Flexural Modulus | 8.27 - 10.3 GPa | 1200 - 1500 ksi | ASTM D790 |
Mar-Bal MB2000-8 Thermoset Polyester Composite Molding Compound An excellent flame and track resistant material with excellent electrical and mechanical properties. Good dielectric strength and low shrink for close dimensional control.Mar-Bal standard grades can.. |
|||
Flexural Modulus | 8.96 - 10.3 GPa | 1300 - 1500 ksi | |
Bulk Molding Compounds BMC T44 High Strength Mineral Filled Molding Compound BMC T44 is a high strength mineral filled molding compound that is available in a variety of colors. It can be injection, compression or transfer molded. BMC T44 has been successful in displacing .. |
|||
Flexural Modulus | 8.96 - 10.3 GPa | 1300 - 1500 ksi | |
Bulk Molding Compounds BMC T44-15613 High Strength Mineral Filled Molding Compound BMC T44-15613 is a high strength mineral filled molding compound that is available in a variety of colors. It can be injection, compression or transfer molded. BMC T44 has been successful in displ.. |
|||
Flexural Modulus | 8.96 - 10.3 GPa | 1300 - 1500 ksi | |
Bulk Molding Compounds BMC 1423 Wear Resistant, Electrical Grade BMC 1423 is a wear-resistant electrical grade material used in applications where there are moving parts. Best anti-wear properties are exhibited when used in conjunction with mating parts molded fr.. |
|||
Flexural Modulus | 8.96 - 10.3 GPa | 1300 - 1500 ksi | |
Bulk Molding Compounds BMC T10(14) General Purpose Molding Compound BMC T10(14) is a general purpose, low shrink molding compound. Due to the excellent flow and controlled reactivity, BMC T10(14) is well suited for injection, transfer or compression molding of intr.. |