Polymer Property : Flexural Modulus = 13.0 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Modulus 10.0 - 13.0 GPa
1450 - 1890 ksi
Compression; ISO 178
Raschig Group DECAL® 937 Phenolic
Mica reinforced phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (W..
Flexural Modulus 10.0 - 13.0 GPa
1450 - 1890 ksi
Compression; ISO 178
Raschig Group RALUPOL® 4806 UP
Glass-fiber reinforced polyester molding compound. Very low mold shrinkage and post-shrinkage, very good mechanical strength, very good electrical values, better performance values compared to UP 80..
Flexural Modulus 12.0 - 13.0 GPa
1740 - 1890 ksi
ISO 178
Perstorp Compounds Aminel GF Melamine
Fiberglass-reinforced melamine material with high dimensional stability, excellent injection properties and high thermal stabilityInformation provided by Perstorp Compounds Inc.
Flexural Modulus 4.90 - 13.0 GPa

@Temperature 100 - 175 °C
711 - 1890 ksi

@Temperature 212 - 347 °F
Average value: 7.76 GPa Grade Count:1
Overview of materials for Polyphthalamide (PPA), 50% Glass Fiber Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Polyphthalamide, 50% Glass Fiber Reinforced". Each property range of values reported is minimum and maxi..
Flexural Modulus 11.0 - 13.0 GPa
1600 - 1890 ksi
ISO 178
Raschig Group 3572 Epoxy
Glass-fiber reinforced epoxy molding compound. Good mechanical strength and electrical strength, enhanced elasticity for ensuring good sealing under extreme heat and/or humidity, good chemical resis..
Flexural Modulus 10.0 - 13.0 GPa
1450 - 1890 ksi
Compression; ISO 178
Raschig Group SURAPLAST 54 UPA
Glass fiber reinforced polyester molding compound. Minimal mold shrinkage and post-shrinkage, very good arc resistance, very good mechanical strength. This product meets the allowed upper limits for..
Flexural Modulus 13.0 - 13.0 GPa

@Temperature 80.0 - 80.0 °C
1890 - 1890 ksi

@Temperature 176 - 176 °F
Average value: 13.0 GPa Grade Count:2
Overview of materials for Nylon 66/6, 60% Glass Fiber Reinforced
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66/6, 60% Glass Fiber Reinforced". Specific grades with glass content between 55% and 64% are incl..
Flexural Modulus 9.00 - 13.0 GPa
1310 - 1890 ksi
ISO 178
Bulk Molding Compounds tetra-DUR F 4401 Bulk Molding Compound
UL-licensed, general purpose productTypical Applications - Requiring mechanical strength, abrasion resistance, dimensional stability, electrical insulation, electrostatic dissipation (explosion prot..
Flexural Modulus 11.0 - 13.0 GPa
1600 - 1890 ksi
Compression; ISO 178
Raschig Group DECAL® 152CL Phenolic
Glass-fiber and mineral reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meet..