Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.806 GPa | 117 ksi | Method 1, Proc. B; ASTM D-790-95 |
Multibase Multi-Pro® 0001 Black Polypropylene This product was specially designed for one customer's extrusion application needs. Data is taken from sample material only.Data provided by Multibase. |
|||
Flexural Modulus | 0.804 GPa | 117 ksi | ASTM D790 |
Braskem LH 437 LMDPE Cast Film Extrusion Polyethylene
(discontinued **) Applications: Diapers (back sheet); Absorbent pads (back sheet). Information provided by Braskem |
|||
Flexural Modulus | 0.810 GPa | 117 ksi | 1% secant at 0.05 in/min; ASTM D790A |
LyondellBasell Pro-fax PF531 Polypropylene Homopolymer, Radiation Resistant Primary Processing Method: Injection MoldingKey Features: high melt flow, radiation-resistant polypropylene homopolymer resin, excellent retention of physical properties and color after radiation st.. |
|||
Flexural Modulus | 0.810 GPa | 117 ksi | 2% Secant-Method 1; ASTM D790 |
Ineos K44-08-123 HDPE Copolymer with Carbon Black Fortiflex® K44-08-123 is a black high density polyethylene copolymer designed specifically for extrusion of potable water, industrial, and mining pipe. It has NSF certification and is recognized.. |
|||
Flexural Modulus | 0.810 GPa | 117 ksi | 2% secant; ASTM D790-02 |
Ipiranga Petrochem GM 9245 F HDPE IPQ produces High Density Polyethylene (HDPE) for use by different segments of the plastics molding industry in several processes, including blow molding, extrusion and injection molding.To produce .. |
|||
Flexural Modulus | 0.810 GPa @Strain <=0.250 % |
117 ksi @Strain <=0.250 % |
ISO 178 |
Total MDPE HR 515 Medium Density Polyethylene, Blown Film MDPE HR 515 is a medium density polyethylene produced with hexene as a co-monomer. It shows a broad molecular weight distribution ensuring outstanding processability.MDPE HR 515 is especially dedic.. |
|||
Flexural Modulus | 0.810 GPa | 117 ksi | cond; ISO 178 |
DSM Novamid® 1011CH5KR PA6 Heat Stabilized, Easy Molding Grade |
|||
Flexural Modulus | 0.810 GPa @Temperature 93.0 °C |
117 ksi @Temperature 199 °F |
ASTM Test |
BASF Ultramid® 8260 40% Mineral Filled PA6 (Dry) Ultramid 8260 is a 40% mineral reinforced PA6 injection molding compound. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low.. |
|||
Flexural Modulus | 0.810 GPa | 117 ksi | ASTM D790 |
Ashley Polymers Ashlene® 733LD Nylon 6 A modified injection molding grade nylon for applications requiring flexibility.Data provided by the manufacturer |