Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 1.29 GPa | 188 ksi | ASTM D790 |
PolyMirae Moplen 342R Injection Molding Grade Polypropylene Moplen RP342R is the polypropylene random copolymer manufactured by PMC under the license of BASELL using the Spheripol process. Moplen RP342R is a random copolymer particularly suitable for injecti.. |
|||
Flexural Modulus | 1.29 - 8.00 GPa | 186 - 1160 ksi | Average value: 5.61 GPa Grade Count:3 |
Overview of materials for PCT, 40% Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PCT, 40% Glass Reinforced". Specific grades with glass content between 35% and 44% are included. Each pr.. |
|||
Flexural Modulus | 1.29 GPa | 187 ksi | 2% Secant, Injection Molded Sample, 0.05 in/min test speed; ASTM D790 |
Ineos N00N-00 Polypropylene Impact Copolymer Grade N00N-00 is a fractional melt flow rate, high impact copolymer polypropylene specifically designed for non-pressure structured wall pipe but can also be used in other extrusion applications req.. |
|||
Flexural Modulus | 1.29 GPa | 187 ksi | 1% secant; ASTM D790-02 |
Ipiranga Petrochem PCC 2314 Polypropylene The production of polypropylene (PP) employs Spheripol technology from Montell / Italy. This technology has been acclaimed all over the world and is known as clean technology, because it does not pr.. |
|||
Flexural Modulus | 1.29 GPa | 187 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman POLYAXIS® PD2000 Polypropylene DescriptionPolyaxis PD 2000 is a polypropylene specifically designed from rotational molding.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and E.. |
|||
Flexural Modulus | 1.29 GPa | 187 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman POLYAXIS® PD2000 Polypropylene DescriptionPolyaxis PD 2000 is a polypropylene specifically designed from rotational molding.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and E.. |
|||
Flexural Modulus | 1.29 GPa | 187 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman POLYAXIS® PD2000 Polypropylene DescriptionPolyaxis PD 2000 is a polypropylene specifically designed from rotational molding.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and E.. |
|||
Flexural Modulus | 1.29 GPa | 187 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman POLYAXIS® PD2000 Polypropylene DescriptionPolyaxis PD 2000 is a polypropylene specifically designed from rotational molding.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and E.. |
|||
Flexural Modulus | 1.29 GPa | 187 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman POLYAXIS® PD2000 Polypropylene DescriptionPolyaxis PD 2000 is a polypropylene specifically designed from rotational molding.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and E.. |
|||
Flexural Modulus | 1.29 GPa | 187 ksi | ISO 178 |
Cathay PA514 Renewable Engineering Polyamide Cathay engineering polyamides contain 26-100% renewably sourced material. Advantages: Operates at similar conditions to PA66; Suitable for injection, compounding and extrusion; Stable mechanical pr.. |
|||
Flexural Modulus | 1.29 GPa | 187 ksi | ASTM D-790 |
Bapolene® 3257U Polyethylene, Injection Molding Bapolene 3257U is a high density polyethylene resin that offers improved cycle times, superior modulus and impact resistance. It complies with US FDA 21CFR177.1520 and has a UV protection package.A.. |
|||
Flexural Modulus | 1.29 GPa | 187 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman POLYAXIS® PD2000 Polypropylene DescriptionPolyaxis PD 2000 is a polypropylene specifically designed from rotational molding.NOTE: Physical properties are based on rotationally molded samples from unpigmented resin. Density and E.. |