Polymer Property : Flexural Modulus = 1.02 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Flexural Modulus 1.02 GPa
148 ksi
STN EN ISO 178
Plastcom PLASTALEN® PQ 81 T 15/1 Polypropylene reinforced with mineral filler, impact modified
Modified PP for injection molding with the content of 15% mineral filler. Application in automotive industry. Delivered in black grade.Information Provided by Plastcom spol. s r.o.
Flexural Modulus 1.02 GPa
148 ksi
Plastcom SLOVALEN PQ 81 T 15 PP, 15% mineral filling
FeaturesModified PP for injection moulding with the content of 15% mineral filling. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. Gene..
Flexural Modulus 1.02 - 4.55 GPa
148 - 660 ksi
Average value: 2.03 GPa Grade Count:39
Overview of materials for Polypropylene, Mineral Reinforced, Impact Modified
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Mineral Reinforced, Impact Modified". Each property range of values reported is minimum a..
Flexural Modulus 1.02 - 4.10 GPa
148 - 595 ksi
Average value: 2.08 GPa Grade Count:301
Overview of materials for Polypropylene with 20% Talc Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 20% Talc Filler".Specific grades with primary filler content between 15% and 24% are ..
Flexural Modulus 1.02 GPa
148 ksi
1.3 mm/min, 50 mm span; ASTM D790
SABIC Innovative Plastics LNP STAT-KON MX12407C PP
LNP* STAT-KON* MX12407C is a compound based on Polypropylene resin containing Proprietary Filler(s). Added features of this material include: Electrically Conductive, Clean Compounding System.
Flexural Modulus 1.02 GPa
148 ksi
ASTM D790
UBE UBESTA® P3014UMX Powder Electronic Grade Nylon 12
Description: UBESTA Nylon 12 has an excellent termite resistance than other plastics. UBESTA contributes as a material for jacket and sheath which lay for telephone and telegram Communication System..
Flexural Modulus 1.02 GPa
148 ksi
2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B
Dow DMDA-8940 NT 7 High Density Polyethylene Resin
DOW DMDA-8940 NT 7 is produced using UNIPOL™ process technology. It is intended for use in a broad range of injection molding applications such as housewares, toys, food containers and pails. Info..
Flexural Modulus 1.02 GPa
148 ksi
ASTM D790A
Dow DT702 TPO
Dow Fascia TPO for Painted ApplicationsInformation provided by Dow
Flexural Modulus 1.02 GPa
148 ksi
2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B
Dow UNIVAL™ DMDC-6143 NT 7 High Density Polyethylene Resin (HDPE)
Excellent parison melt strength / low sag Good extrudability / process-ability Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a UNIVAL™ DMDC-6143 NT 7 is a polymer with broad molecular weight distri..
Flexural Modulus 1.02 GPa
148 ksi
2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B
Dow UNIVAL™ DMDD-6200 NT 7 High Density Polyethylene Resin (HDPE)
Moderate swell Complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a UNIVAL™ DMDD-6200 NT 7 is a multipurpose polymer designed for the high speed production of blow molded containers used to package hous..
Flexural Modulus 1.02 GPa
148 ksi
1% Secant; ASTM D790
Amco PRIMATOP PP CO 350-20 Impact Polypropylene Copolymer
PP CO 350-20 has easy mold flow and excellent dimensional stability. It is used in thin walled injection molded applications.Former A-Top Polymers product; part of Amco product line since 2013.