Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.524 GPa | 76.0 ksi | Method I (3 point load), Procedure B); ASTM D790 |
Multibase Multi-Flex® D 5308 HF Black TPO Thermoplastic Polyolefin Elastomer Forms: PelletsInformation provided by Multibase |
|||
Flexural Modulus | 0.524 GPa | 76.0 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
Dow DNDA-1081 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-1081 NT 7 is produced using UNIPOL™ PE process technology. It is intended for high-speed injection molding of thin walled parts such as downguaged lids. Information provided by Dow |
|||
Flexural Modulus | 0.524 GPa | 76.0 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
Dow DNDA-1149 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-1149 NT 7 is produced using UNIPOL™ PE process technology and is intended for high-speed injection molding applications. Information provided by Dow |
|||
Flexural Modulus | 0.524 GPa | 76.0 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
Dow DNDA-9810 NT 7 Linear Low Density Polyethylene Resin DOW DNDA-9810 NT 7 is produced using UNIPOL™ PE process technology and is supplied in pellet form. This resin is specifically designed as a carrier resin for color concentrates and other masterbat.. |
|||
Flexural Modulus | 0.524 GPa | 76.0 ksi | 2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B |
Dow DNDB-1077 NT 7 Linear Low Density Polyethylene Resin DOW DNDB-1077 NT 7 is produced using UNIPOL™ PE process technology. It is intended for high-speed injection molding of thin walled parts such as downguaged lids. Information provided by Dow |