Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.207 GPa | 30.0 ksi | method 1, Proc.B; ASTM D-790 |
Multibase Multi-Flex® TPE D 4201 BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | 2% Secant; ASTM D 790 |
Chevron Phillips 1006 LDPE Injection Molding Resin
(discontinued **) Resin Type: homopolymerCharacteristics: excellent flexibility, excellent flow, good warping resistance, moderate mold release, moderate ESCRApplications: large housewares, tamper evident snap-on cap.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | 2% Secant, 12.7 mm/min. (0.5 in./min.); ASTM D790 |
Eastman 1550A Polyethylene
(discontinued **) Injection molding gradeUnless otherwise noted, all tests are run at 23°C and 50% RH. Where required, samples are compression molded per ASTM D1928.Information from manufacturer data sheet.Eastman .. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | 2% Secant, 12.7 mm/min. (0.5 in./min.); ASTM D790 |
Eastman 1550P Polyethylene
(discontinued **) Injection molding gradeUnless otherwise noted, all tests are run at 23°C and 50% RH. Where required, samples are compression molded per ASTM D1928.Information from manufacturer data sheet.Eastman .. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | 2% Secant, 12.7 mm/min. (0.5 in./min.); ASTM D790 |
Eastman 1830A Polyethylene
(discontinued **) Polyethylene 1830A is a low density formulation. It is suggested for injection molding applications requiring good stiffness or gloss properties . It us used in applications such as closures.Polyet.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | 2% Secant, 12.7 mm/min. (0.5 in./min.); ASTM D790 |
Eastman 1830E Polyethylene
(discontinued **) Polyethylene 1830E is a low density formulation. It is suggested for general purpose extrusion applications, such as tubing and blow molding. Polyethylene 1830E meet the requirements of FDA regula.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | 2% Secant, 12.7 mm/min. (0.5 in./min.); ASTM D790 |
Eastman 1870A Polyethylene
(discontinued **) Polyethylene 1870A is a low density formulation with excellent flow characteristics for injection molding. It is used for such applications as container closures that require stress-crack resistanc.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | 2% Secant, 12.7 mm/min. (0.5 in./min.); ASTM D790 |
Eastman 808A Polyethylene
(discontinued **) Low density polyethylene 808A is a general-purpose formulation used for injection molding and general-purpose extrusion.Unless otherwise noted, all tests are run at 23°C and 50% RH.Information from.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | 2% Secant, 12.7 mm/min. (0.5 in./min.); ASTM D790 |
Eastman 808P Polyethylene
(discontinued **) Low density polyethylene 808P is a low density resin designed for applications, such as sugar pouches and freezer wrap, where high coating speeds and good drawdown are required. The combination of .. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | ASTM D790 |
3M Dyneon™ THV™ 500 Fluorothermoplastic
(discontinued **) Data provided by the manufacturer, Dyneon LLC.This unique, melt-processable, tetrafluoroethylene, hexafluoropropylene, and vinylidene fluoride (THV) terpolymer provides a unique combination of perf.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | ASTM D790 |
Multibase Multi-Flex® D 3104-8 TPO Thermoplastic Polyolefin Elastomer Features: Chemical Resistance, Good PaintableOzone Resistant Thermal Stability, GoodDensity, LowTear Strength, GoodScratch Resistant Forms:PelletsProcessing Method:Injection Molding Uses: Automot.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | ASTM D790 |
Techmer ES HiFill® TPU 0266 A Availability: North AmericaForms: PelletsFeatures: High Density and High Specific GravityInformation provided by TP Composites, Inc. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene DescriptionCP 763-01 is an extruded, blow molding, and injection molding grade of low density polyethylene having good processability and heat sealability. ApplicationCP 763-01 meets the specificat.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene DescriptionCP 763-01 is an extruded, blow molding, and injection molding grade of low density polyethylene having good processability and heat sealability. ApplicationCP 763-01 meets the specificat.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | ASTM D790 |
Westlake Plastics Clariflex® TFE/VF2/HFP Clariflex is a flexible, transparent fluoroplastic composed of tetrafluoroethylene, hexafluoro-propylene, and vinylidene fluoride. Notable properties include light transmission, chemical resistance.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene DescriptionCP 763-01 is an extruded, blow molding, and injection molding grade of low density polyethylene having good processability and heat sealability. ApplicationCP 763-01 meets the specificat.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene DescriptionCP 763-01 is an extruded, blow molding, and injection molding grade of low density polyethylene having good processability and heat sealability. ApplicationCP 763-01 meets the specificat.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene DescriptionCP 763-01 is an extruded, blow molding, and injection molding grade of low density polyethylene having good processability and heat sealability. ApplicationCP 763-01 meets the specificat.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | at 1% secant modulus; ASTM D790 |
A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene DescriptionCP 763-01 is an extruded, blow molding, and injection molding grade of low density polyethylene having good processability and heat sealability. ApplicationCP 763-01 meets the specificat.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | ASTM D790 |
AdvanSource Biomaterials ChronoFlex® C 75D Biodurable Medical Grade Polyurethane ChronoFlex® C is a family of premium polycarbonate aromatic biodurable thermoplastic polyurethane elastomers developed by AdvanSource Biomaterials Corporation. ChronoFlex® C medical-grade elastome.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | ASTM D790 |
Dow PELLETHANE® 2104-65D Polyurethane Elastomer (Ether-Ether Hybrid)
(discontinued **) Description: PELLETHANE® 2104-65D Polyester based. Excellent oil and chemical resistance. Applications include: Caster wheels, Seals, Gaskets, Animal tags, Hose jacketing, Ski boots, AutomotiveDat.. |
|||
Flexural Modulus | 0.207 GPa | 30.0 ksi | 2% Secant, 12.7 mm/min. (0.5 in./min.); ASTM D790 |
Eastman D4042-P Polyethylene
(discontinued **) D4042-P is a low density resin designed for applications such as sugar pouches and freezer wrap, where high coating speeds and good drawdown are required. The combination of high melt index and low.. |