Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Flexural Modulus | 0.180 GPa | 26.1 ksi | ISO 178 |
Polimeri Europa Riblene® MR 30 Low Density Polyethylene - Injection Molding Riblene MR 30 is a high fluidity low density polyethylene resin (LDPE) characterized by a high flowability and a medium rigidity.Parts made with Riblene MR 30 are characterized by good mechanical an.. |
|||
Flexural Modulus | 0.180 - 1.77 GPa | 26.1 - 257 ksi | Average value: 0.835 GPa Grade Count:16 |
Overview of materials for Thermoplastic Olefinic Elastomer (TPO), Extrusion Grade This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Olefinic Elastomer (TPO), Extrusion Grade". Each property range of values reported is mini.. |
|||
Flexural Modulus | 0.180 GPa | 26.1 ksi | ISO 178 |
FKuR Kunststoff Terralene® LL 1303 Biobased Polyethylene With the brand name Terralene® FKuR offers biobased polyethylene compounds made using Braskem's Green PE. When compared to conventional polyethylene (PE), the main difference is that the ethanol.. |
|||
Flexural Modulus | 0.180 GPa | 26.1 ksi | 12.5 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL WCP921 PPE-TPE Flexible Noryl* injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain relief.. |
|||
Flexural Modulus | 0.180 GPa | 26.1 ksi | 12.5 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL WCP921 PPE-TPE (Asia Pacific) Flexible Noryl* injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain relief.. |
|||
Flexural Modulus | 0.180 GPa | 26.1 ksi | 12.5 mm/min, 100 mm span; ASTM D790 |
SABIC Innovative Plastics NORYL WCP921 PPE-TPE (Europe-Africa-Middle East) Flexible Noryl* injection molding grade. Low specific gravity with good non-halogenated flame retardant performance. Developed for evaluation in overmolding applications such as plugs, strain relief.. |
|||
Flexural Modulus | 0.180 GPa | 26.1 ksi | 2 mm/min; ISO 178 |
SABIC Innovative Plastics LNP LUBRICOMP YI001 Polyester Elastomer (Europe-Africa-Middle East) LNP* LUBRICOMP* YI001 is a compound based on Polyester Elastomer containing Silicone. Added features include; Internally Lubricated. |
|||
Flexural Modulus | 0.180 GPa | 26.1 ksi | ISO 178 |
Ecomass® 1002ZD93 Tungsten Filled COPA Nontoxic alternative to Lead (Pb), weighting, balancing and radiation shielding applicationsHigh Specific GravityTungsten Powder Filled Co-Polyamide (COPA)Excellent ToughnessInformation provided by .. |
|||
Flexural Modulus | 0.180 GPa | 26.1 ksi | Conditioned 15 days at 23°C - 50% RH; ISO 178 |
Arkema Group Pebax® MP 1878 SP 01 Polyether Block Amide (PEBA) Polyether block amide PEBAX® MP 1878 SP 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. Added to PA6 Pebax® MP 1878 enhances the properties of PA6, especially at lo.. |
|||
Flexural Modulus | 0.180 GPa | 26.1 ksi | ASTM D790 |
C.O.I.M. LARIPUR® LPR5520 Standard Adipate Ester Polyurethane Description: The products of the LARIPUR® line are thermoplastic polyurethanes. These products combine the technology of thermoplastic products with the features of polyurethanes:Excellent abrasion.. |
|||
Flexural Modulus | 0.180 GPa | 26.1 ksi | Conditioned 15 days at 23°C - 50% RH; ISO 178 |
Arkema Group Pebax® MP 1878 SA 01 Polyether Block Amide (PEBA) Polyether block amide PEBAX® MP 1878 SA 01 is a thermoplastic elastomer made of flexible polyether and rigid polyamide. Added to PA6 Pebax® MP 1878 enhances the properties of PA6, especially at lo.. |