Polymer Property : Flexural Modulus = 23.4 GPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Flexural Modulus	23.4 GPa @Temperature 23.9 °C	3400 ksi @Temperature 75.0 °F	Dry; ASTM D790
Park Electrochemical Nelcote® E-720 Epoxy Prepreg, 581 Quartz Reinforced Nelcote® E-720 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-720 has a proven history in many demanding aerospac..
Flexural Modulus	23.4 GPa @Temperature 23.9 °C	3400 ksi @Temperature 75.0 °F	Dry; ASTM D790
Park Electrochemical Nelcote® E-720 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-720 is a modified epoxy resin system designed to retain excellent mechanical properties after extended exposure to high temperature. E-720 has a proven history in many demanding aerospac..
Flexural Modulus	23.4 GPa @Temperature 87.8 °C	3400 ksi @Temperature 190 °F	Dry; ASTM D790
Park Electrochemical Nelcote® E-722 Epoxy Prepreg, 285 Kevlar® Reinforced Nelcote® E-722 is a modified 350°F cure epoxy system with excellent processing characteristics for vacuum bag, press, and autoclave molding.Key Features and Benefits:Epoxy resin system optimized f..
Flexural Modulus	23.4 GPa @Temperature 93.3 °C	3400 ksi @Temperature 200 °F	Dry; ASTM D790
Park Electrochemical Nelcote® E-761 Epoxy Prepreg, 285 Kevlar® Reinforced Nelcote® E-761 is a versatile self-adhesive epoxy matrix for use in aerospace and commercial application where ease of processing and cost are key considerations.Key Features and Benefits:Controlle..
Flexural Modulus	23.4 GPa @Temperature 23.9 °C	3400 ksi @Temperature 75.0 °F	Dry; Oven Cure 250°F, 90 min; ASTM D790
Park Electrochemical Nelcote® E-763 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-763 is a modified epoxy system with a nominal 250°F cure temperature. E-763 provides a transparent resin surface on the finished part which gives finished part surfaces a cosmetic attra..
Flexural Modulus	23.4 GPa @Temperature 71.1 °C	3400 ksi @Temperature 160 °F	Dry; Oven Cure 250°F, 90 min; ASTM D790
Park Electrochemical Nelcote® E-763 Epoxy Prepreg, 7781 E-Glass Reinforced Nelcote® E-763 is a modified epoxy system with a nominal 250°F cure temperature. E-763 provides a transparent resin surface on the finished part which gives finished part surfaces a cosmetic attra..
Flexural Modulus	23.4 GPa @Temperature 23.9 °C	3400 ksi @Temperature 75.0 °F	Dry; ASTM D790
Park Electrochemical Nelcote® P-600 Polyester Prepreg, 7781 E-Glass Reinforced Nelcote® P-600 is a general purpose 190°F curing polyester system widely accepted as a cost-effective alternative to wet lay-up processingKey Features and Benefits:Meets MIL-R-7575 requirements160..
Flexural Modulus	23.4 GPa @Temperature 23.9 °C	3400 ksi @Temperature 75.0 °F	Wet; ASTM D790
Park Electrochemical Nelcote® P-670I Polyester Prepreg, 7781 E-Glass Reinforced Nelcote® P-670I is a versatile, non-styrenated/low VOC polyester resin. P670I is used in a wide variety of applications including radomes, tooling and aircraft structures.Key Features and Benefits:..
Flexural Modulus	23.4 GPa @Temperature 23.9 °C	3400 ksi @Temperature 75.0 °F	0° Direction, Dry; ASTM D790
Park Electrochemical Nelcote® V-376 Cyanate Ester Epoxy Prepregs, 7781 E-Glass Reinforced Nelcote® V-376 is a Cyanate Ester matrix providing excellent electrical and mechanical properties for harsh aircraft, shipboard, and undersea applications for Radomes, Antenna, and Reflectors. Simp..
Flexural Modulus	23.4 GPa @Temperature 23.0 °C	3390 ksi @Temperature 73.4 °F
Hexcel® HexPly® F515 Epoxy Resin, 7781 Glass Fabric Hexcel designation: 7781-38"-F515; Fiber 75-1/0Information provided by HexCel