Polymer Property : Tensile Creep Modulus, 1000 hours = 479000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Creep Modulus, 1000 hours	3300 - 7400 MPa	479000 - 1.07e+6 psi	Average value: 5760 MPa Grade Count:5
Overview of materials for PBT + ASA Blend, Glass Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "PBT + ASA Blend, Glass Fiber Reinforced". Each property range of values reported is minimum and maximum ..
Tensile Creep Modulus, 1000 hours	3300 MPa	479000 psi	ISO 899-1
Lanxess DurethanÂ® BKV 130 000000 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 30, even in..
Tensile Creep Modulus, 1000 hours	3300 MPa	479000 psi	ISO 899-1
Lanxess DurethanÂ® BKV 130 H2.0 901510 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer-modified, electroplateable, improved notched impact strength and energy absorption under biaxial impact load, good heat-ageing resistance
Tensile Creep Modulus, 1000 hours	3300 MPa	479000 psi	ISO 899-1
Lanxess DurethanÂ® BKV 130 H3.0 101006 Copolyamide, 30% Glass Fiber CoPA, injection molding grade, 30% glass fibers, elastomer-modified, electroplateable, higher notched impact strength and also higher energy absorption under biaxial impact load than BKV 30 H3.0, ev..
Tensile Creep Modulus, 1000 hours	3300 MPa @Strain <=0.500 %	479000 psi @Strain <=0.500 %	ISO 899-1
BASF Ultradur® S 4090 G2 10% Glass Filled PBT Description: Is a PBT + ASA, easy-flowing injection-molding grades with 10% glass fibers; for rigid, tough and dimensionally stable technical parts e. g. housings, consoles, contact carriers, covers..
Tensile Creep Modulus, 1000 hours	3300 MPa @Strain <=0.500 %	479000 psi @Strain <=0.500 %	ISO 899-1
BASF Ultramid® B3EG7 35% Glass Filled PA6 (Conditioned) Description: 35% Glass fiber reinforced injection molding grade for industrial articles and electrical insulating parts.Information provided by BASF
Tensile Creep Modulus, 1000 hours	3300 MPa @Strain <=0.500 %	479000 psi @Strain <=0.500 %	ISO 899-1
BASF Ultramid® B3EG7 BK 00564 35% Glass Filled PA6 (Conditioned) Description: 35% Glass fiber reinforced injection molding grade for industrial articles and electrical insulating parts.Information provided by BASF
Tensile Creep Modulus, 1000 hours	3300 MPa @Strain <=0.500 %	479000 psi @Strain <=0.500 %	ISO 899-1
BASF Ultramid® B3WG7 BK 00564 35% Glass Filled PA6 (Conditioned) Description: 35% glass-fiber reinforced and heat aging resistant injection-molding grade, e.g. for automotive manifolds and pedals.Information provided by BASF