Polymer Property : Tensile Creep Modulus, 1000 hours = 392000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Creep Modulus, 1000 hours	2700 MPa	392000 psi	ISO 899-1
Lanxess PocanÂ® B 7375 000000 PBT, White Pigment PBT, 25% white pigments, injection molding, improved light reflection, low tendency to warp
Tensile Creep Modulus, 1000 hours	2700 MPa	392000 psi	ISO 899-1
Lanxess PocanÂ® B 7425 000000 PBT, 20% Glass Spheres PBT, 20% glass spheres, injection molding, low tendency to warp, improved surface finish
Tensile Creep Modulus, 1000 hours	2700 MPa @Strain <=0.500 %	392000 psi @Strain <=0.500 %	ISO 899-1
BASF Ultrason® E 2010 MR SW 10111 PESU Description: Unreinforced, medium viscosity standard injection molding grade, demolding optimized. Abbreviated designation according to ISO 1043-1: PESU.Information provided by BASF
Tensile Creep Modulus, 1000 hours	2700 MPa	392000 psi	ISO 899-1
BASF Ultrason® E 3010 MR UN PESU Description: Unreinforced, higher viscosity injection molding and extrusion grade with improved toughness and chemical resistance (stress crack resistance); demolding optimized. Abbreviated designat..
Tensile Creep Modulus, 1000 hours	2700 MPa	392000 psi	elongation <0.5%, 23°C; ISO 899-1
BASF Ultrason E 1010 PES Ultrason E 1010 is an unreinforced, low viscosity injection molding PES grade. It flows readily and offers outstanding heat resistance and dimensional stability.
Tensile Creep Modulus, 1000 hours	2700 MPa	392000 psi	elongation <0.5%, 23°C; ISO 899
BASF Ultrason E 2010 PES Ultrason E 2010 is an unreinforced, medium viscosity standard injection molding PES grade. It flows readily and offers outstanding heat resistance and dimensional stability. It conforms to FDA req..
Tensile Creep Modulus, 1000 hours	2700 MPa @Strain <=0.500 %	392000 psi @Strain <=0.500 %	ISO 899-1
BASF Ultrason® E 2010 HC PESU Information provided by BASF
Tensile Creep Modulus, 1000 hours	2700 - 8300 MPa	392000 - 1.20e+6 psi	Average value: 3760 MPa Grade Count:8
Overview of materials for Polyethersulfone (PES) This property data is a summary of similar materials in the MatWeb database for the category "Polyethersulfone". Each property range of values reported is minimum and maximum values of appropriate M..