Polymer Property : Tensile Creep Modulus, 1000 hours = 1700 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Creep Modulus, 1000 hours 1700 - 5400 MPa
247000 - 783000 psi
Average value: 2090 MPa Grade Count:25
Overview of materials for Polycarbonate, Unreinforced, Flame Retardant
This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Unreinforced, Flame Retardant". Each property range of values reported is minimum and max..
Tensile Creep Modulus, 1000 hours 1700 MPa
247000 psi
Arkema Group Oroglas® MI-2T Acrylic  (discontinued **)
OROGLAS MI-2T is an injection molding acrylic grade that offers excellent thermal resistance with slight improvement in impact performance.Key features improved deformation and toughness : up to 2..
Tensile Creep Modulus, 1000 hours 1700 MPa
247000 psi
Covestro Bayblend® T 85 MN Polycarbonate/ABS Blend
High impact and notched impact strength, little risk of brittle fracture, high dimensional accuracy.Applications: Automotive components, electrical engineering.Information provided by Bayer.As of 1 ..
Tensile Creep Modulus, 1000 hours 1700 MPa
247000 psi
Covestro Makrolon® 2205 Polycarbonate, Injection Grade
Exceptionally good flow injection molding grade with easy mold release, for parts with a low wall thickness and long flow paths.Information provided by Bayer.As of 1 September 2015, Bayer MaterialSc..
Tensile Creep Modulus, 1000 hours 1700 MPa
247000 psi
Covestro Makrolon® 2207 Polycarbonate, Injection Grade
Exceptionally good flow injection molding grade with easy mold release and UV stabilizer, for parts with a low wall thickness and long flow paths.Information provided by Bayer.As of 1 September 2015..
Tensile Creep Modulus, 1000 hours 1700 MPa
247000 psi
ISO 899-1
Covestro Makrolon® 2258 Polycarbonate
Main characteristics:• High toughness• Good heat resistance• Glass-like transparency, optical quality• High dimensional accuracy and stabilityGrade characteristics:• Medical devices - bioc..
Tensile Creep Modulus, 1000 hours 1700 MPa

@Temperature 23.0 °C
247000 psi

@Temperature 73.4 °F
ISO 899
DuPont Performance Polymers Delrin® 111P NC010 Acetal Homopolymer
Delrin® 111P is a high viscosity acetal homopolymer with improved thermal stability and modifications for more precise molding (reduced warpage, fewer voids). It has higher tensile strength and mod..
Tensile Creep Modulus, 1000 hours 1700 MPa
247000 psi
BASF Polystyrol® 454 C Impact Grade Polystyrene (Europe)
Easy flowing, medium-impact grade.Data was collected by ISO methods and provided by BASF.
Tensile Creep Modulus, 1000 hours 1700 MPa
247000 psi
ISO 899-1
Covestro Makrolon® LED2245 Polycarbonate
ISO 7391-PC,MRT,(,,)-24-9Global gradeFormerly Makrolon DP1-1857MVR (300 °C/1.2 kg) 36 cm3/10 minLight guidesPC with highest transmissionLow viscosityEasy releaseInjection molding - Melt temperature..
Tensile Creep Modulus, 1000 hours 1700 MPa
247000 psi
Arkema Group Oroglas® V 045 I Acrylic, Extrusion Grade  (discontinued **)
OROGLAS V 045 I is an extrusion that exhibits the following properties : 50% tougher than standard acrylics excellent optical properties ( comparable to that of standard acrylics) superior surface ..