Polymer Property : Tensile Creep Modulus, 1000 hours = 116000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Creep Modulus, 1000 hours	800 - 1600 MPa	116000 - 232000 psi	Average value: 1480 MPa Grade Count:11
Overview of materials for Acetal Homopolymer, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Acetal Homopolymer, Unreinforced". Each property range of values reported is minimum and maximum values ..
Tensile Creep Modulus, 1000 hours	800 - 5200 MPa	116000 - 754000 psi	Average value: 1880 MPa Grade Count:6
Overview of materials for Nylon 6-3 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6-3". Each property range of values reported is minimum and maximum values of appropriate MatWeb e..
Tensile Creep Modulus, 1000 hours	800 MPa	116000 psi	ISO 899-1
Lanxess DurethanÂ® AC 30 000000 Nylon 66 PA 66, injection molding-grade, non-reinforced, higher notched impact strength than A 30 / A 31 in the dry and conditioned stateApplication Examples: plug connectors, cable binders, cable clips, par..
Tensile Creep Modulus, 1000 hours	800 MPa @Time 3.60e+6 sec	116000 psi @Time 1000 hour	ISO 899-1
DuPont Performance Polymers Delrin® 520MP NC010 Acetal (POM) (Unverified Data**) 20% Teflon® Lubricated Medium Viscosity Acetal Homopolymer with Low Wear and Low Friction Delrin 520MP is a medium viscosity acetal homopolymer containing 20% Teflon PTFE Micropowder. It is designe..
Tensile Creep Modulus, 1000 hours	800 MPa @Strain <=0.500 %	116000 psi @Strain <=0.500 %	ISO 899-1
BASF Ultramid® B3M6 BK 23213 30% Mineral Filled PA6 (Conditioned) Description: 30% Mineral-filled injection molding grade for high impact industrial items having very high dimensional stability, such as automobile wheel covers.Information provided by BASF
Tensile Creep Modulus, 1000 hours	800 MPa @Strain 0.500 %	116000 psi @Strain 0.500 %	ISO 899-1
BASF Ultramid® B3M6 BK60564 30% Mineral Filled PA6 (Conditioned) Ultramid B3M6 BK60564 is a 30% mineral reinforced, pigmented black injection molding PA6 grade for industrial items requiring high impact strength and very high dimensional stability, excellent lase..
Tensile Creep Modulus, 1000 hours	800 MPa @Strain <=0.500 %	116000 psi @Strain <=0.500 %	ISO 899-1
BASF Ultramid® B3M6 Grey 22319 Q94 30% Mineral Filled PA6 (Conditioned) Description: 30% Mineral-filled injection molding grade for high impact industrial items having very high dimensional stability, such as automobile wheel covers.Information provided by BASF