Mechanical Properties	Metric	English	Comments
Tensile Creep Modulus, 1000 hours	8500 MPa	1.23e+6 psi	ISO 899-1
Lanxess Pocan® T 7331 POS151 000000 PBT + PET, 30% Glass Fiber (discontinued **) PBT+PET, 30% glass fibers, injection molding, improved surface finish, increased temperature peak load, UV-stabilized
Tensile Creep Modulus, 1000 hours	8500 MPa	1.23e+6 psi	ISO 899-1
Lanxess PocanÂ® T 7331 000000 PBT + PET, 30% Glass Fiber PBT+PET, 30% glass fibers, injection molding, improved surface finish, increased temperature peak load
Tensile Creep Modulus, 1000 hours	8500 MPa	1.23e+6 psi	ISO 899-1
Lanxess PocanÂ® T 7331 POS151 700226 PBT + PET, 30% Glass Fiber PBT + PET, 30% glass fibers, injection molding, improved surface finish, increased temperature peak load, UV stabilizedInformation provided by LANXESS.
Tensile Creep Modulus, 1000 hours	8500 - 10000 MPa	1.23e+6 - 1.45e+6 psi	Average value: 9130 MPa Grade Count:4