Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Heat Seal Strength Initiation Temperature | 103 °C @Thickness 0.0508 mm |
217 °F @Thickness 0.00200 in |
FPC |
Formosa Plastics Formolene® FORMAX® L91507H Film (Hexene Grade) LLDPE
(discontinued **) Superior Performance Linear Low Density Polyethylene for Film Extrusion Formolene FORMAX® L9 is a superior strength linear low density hexene copolymer polyethylene made using a gas-phase process. .. |
|||
Heat Seal Strength Initiation Temperature | 103 °C | 217 °F | 3 N; Borealis Test |
Borealis Borseal™ TD110BF Terpolymer for BOPP Film Borseal TD110BF is a C2/C4 terapolymer film resin.Borseal TD110BF is especially developed for use as sealing layers in coextruded BOPP film (manufactured on Stenter frame and double bubble film proc.. |
|||
Heat Seal Strength Initiation Temperature | 103 °C | 217 °F | 3 N; Borealis Test |
Borealis Borseal™ TD115BF Terpolymer for BOPP Film Borseal TD115BF is a C2/C4 terapolymer film resin.Borseal TD115BF is especially developed for use as sealing layers in coextruded BOPP film (manufactured on Stenter frame and double bubble film proc.. |
|||
Heat Seal Strength Initiation Temperature | 103 °C | 217 °F | 2 N; Borealis Test |
Borealis Borseal™ TD215BF Terpolymer for BOPP Film Borseal TD215BF is a C2/C4 terapolymer film resin.Borseal TD215BF is especially developed for use as sealing layers in coextruded BOPP film (manufactured on Stenter frame and double bubble film proc.. |
|||
Heat Seal Strength Initiation Temperature | 103 °C | 217 °F | 3 N; Borealis Test |
Borealis Borseal™ TD218BF Terpolymer for BOPP Film Borseal TD218BF is a C2/C4 terapolymer film resin.Borseal TD218BF is especially developed for use as sealing layers in coextruded BOPP film (manufactured on Stenter frame and double bubble film proc.. |
|||
Heat Seal Strength Initiation Temperature | 103 °C | 217 °F | 2 N; Borealis Test |
Borealis Borseal™ TD210BF Terpolymer for BOPP Film Borseal TD210BF is a C2/C4 terapolymer film resin especially developed for use as sealing layers in coextruded BOPP film (manufactured on stenter frame and double bubble film process).Borseal TD210B.. |
|||
Heat Seal Strength Initiation Temperature | 103 °C | 217 °F | 2 N; Borealis Test |
Borealis Borseal™ TD211BF Terpolymer for BOPP Film Borseal TD211BF is a C2/C4 terapolymer film resin especially developed for use as sealing layers in coextruded BOPP film (manufactured on stenter frame and double bubble film process).Borseal TD211B.. |
|||
Heat Seal Strength Initiation Temperature | 103 °C | 217 °F | 0.5 s dwell; 2 lb<sub>f</sub>/in |
Bapolene® 152A Polyethylene Film Grade Bapolene 152A is a hexene linear low density polyethylene with a combination of superior impact strength and HSIT. Product is designed to exhibit performance similar to that of metallocene products... |
|||
Heat Seal Strength Initiation Temperature | 103 °C | 217 °F | 0.5 s dwell; 2 lb<sub>f</sub>/in |
Bapolene® 152B Polyethylene Film Grade Bapolene 152B is a hexene linear low density polyethylene with a combination of superior impact strength and HSIT. Product is designed to exhibit performance similar to that of metallocene products... |
|||
Heat Seal Strength Initiation Temperature | 103 °C | 217 °F | 0.5 s dwell; 2 lb<sub>f</sub>/in |
Bapolene® 152F Polyethylene Film Grade Bapolene 152F is a hexene linear low density polyethylene with a combination of superior impact strength and HSIT. Product is designed to exhibit performance similar to that of metallocene products... |