Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 33.1 MPa @Temperature 23.9 °C |
4800 psi @Temperature 75.0 °F |
Short-Beam, Dry; 325°F Autoclave Cured; ASTM D5379 |
Park Electrochemical Nelcote® F-502 Phenolic Prepreg, 3K 8HS PAN Reinforced Nelcote® F-502 is a MIL-R-9299 phenolic resin system suitable for impregnation on any MIL-C-9084 fabric with a compatible finish. F-502 is used in the manufacture of ablative reinforcements in rock.. |
|||
Shear Strength | >= 33.1 MPa | >= 4800 psi | Die |
Parker Chomerics CHO-BOND SV712 Conductive Epoxy CHO-BOND® 700 Series Adhesives for Microelectronics Packaging; these pure silver-filled epoxy pastes are designed to meet the demanding requirements of semiconductor and microelectronic packaging. .. |
|||
Shear Strength | 33.1 MPa | 4800 psi | ASTM D732 |
Quadrant EPP TIVAR® 1000 UHMW-PE, Virgin (ASTM Product Data Sheet) |
|||
Shear Strength | 33.1 MPa | 4800 psi | ASTM D732 |
Quadrant EPP TIVAR® 1000 UV Stabilized UHMW, Black (ASTM Product Data Sheet) |
|||
Shear Strength | 33.1 MPa | 4800 psi | ASTM D732 |
Quadrant EPP TIVAR® 1000 UV Stabilized UHMW-PE, Natural & Colored Except Black (ASTM Product Data Sheet) |
|||
Shear Strength | 33.1 MPa @Temperature 22.8 °C |
4800 psi @Temperature 73.0 °F |
ASTM D732 |
Quadrant EPP TIVAR® 1000 Virgin (Natural & Color except Black) UHMW-PE |
|||
Shear Strength | 33.1 MPa | 4800 psi | ASTM D732 |
Quadrant EPP TIVAR® 88-2 ESD Black, Premium Lubricant Filled, Lower COF, Electro Static Dissipative Lining Material (ASTM Product Data Sheet) |
|||
Shear Strength | 33.1 MPa | 4800 psi | ASTM D732 |
Quadrant EPP TIVAR® 88-2 UHMW-PE, Premium Lubricant Filled Lining Material (ASTM Product Data Sheet) Promotes reliable, steady bulk material flow Abrasion-, chemical- and corrosion-resistant Low coefficient of friction No moisture absorption Reduces or eliminates arching, ratholing and erractic f.. |
|||
Shear Strength | 33.1 MPa | 4800 psi | ASTM D732 |
Quadrant EPP TIVAR® ESD Electro Static Dissipative UHMW-PE (ASTM Product Data Sheet) Protects against electrical charge build-up Reduces noise Self-lubricating Corrosion-resistant No moisture absorption |
|||
Shear Strength | 33.1 MPa | 4800 psi | ASTM D732 |
Quadrant EPP TIVAR® H.O.T. UHMW-PE, Premium Heat Stabilized/Anti-Oxidant Filled, (FDA, USDA, & 3-A Dairy) (ASTM Product Data Sheet) |
|||
Shear Strength | 33.1 MPa | 4800 psi | Average value: 33.1 MPa Grade Count:9 |
Overview of materials for High Density Polyethylene (HDPE), Ultra High Molecular Weight This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Ultra High Molecular Weight". Each property range of values reported i.. |
|||
Shear Strength | 33.1 MPa | 4800 psi | Shear Bond Holding Strength |
Indium Corp. Indalloy® 227 Sn-In-Ag Solder Alloy Pb free solder can be used as a replacement for 63Sn 37Pb, 62Sn 36Pb 2Ag and 60Sn 40Pb in that it has similar physical and mechanical properties. Not for use over 100°C due to 118°C Sn/In eut.. |
|||
Shear Strength | 33.1 MPa | 4800 psi | Overlap, Etched Aluminum tested after 1 week of Immersion in 20% bleach solution |
3M Scotch-Weld™ DP812 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP812 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact, durability and.. |
|||
Shear Strength | 33.1 MPa | 4800 psi | Overlap, Etched Aluminum, RT, 50% for 30 days, Cohesive Failure |
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i.. |
|||
Shear Strength | 33.1 MPa | 4800 psi | Overlap, Etched Aluminum, Diesel Fuel at RT for 30 days immersion, Cohesive Failure |
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i.. |
|||
Shear Strength | 33.1 MPa | 4800 psi | Overlap, Etched Aluminum cured for 7 days @ RT |
3M Scotch-Weld™ DP825 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP825 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact, durability and.. |
|||
Shear Strength | 33.1 MPa | 4800 psi | Aluminum, etched, Overlap, Control, Cohesive Failure |
3M Scotch-Weld™ LSB60 Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60 is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of f.. |
|||
Shear Strength | 33.1 MPa | 4800 psi | Aluminum, etched, Overlap, Control, Cohesive Failure |
3M Scotch-Weld™ LSB60NS Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60NS is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of.. |
|||
Shear Strength | 33.09 MPa | 4800 psi | ASTM D1002-94 |
Aremco Aremco-Bond™ 2320 High Performance Epoxide Toughened, Unfilled, Fast-Setting, BPA Free, 2:1, High Peel & Shear Strength |
|||
Shear Strength | 33.1 MPa | 4800 psi | ASTM D732 |
Quadrant EPP Quicksilver® UHMW-PE Premium Truck Lining (ASTM Product Data Sheet) |