Polymer Property : Shear Strength = 4100 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	28.3 MPa @Temperature 23.9 °C	4100 psi @Temperature 75.0 °F	Short Beam; Dry; ASTM D790
Park Electrochemical Nelcote® V-303 Polyimide Prepreg, 7781 E-Glass Reinforced Nelcote® V-303 is non-MDA condensation polyimide prepreg with a service temperature of 600°F.Key Features and Benefits:600°F maximum service temperatureGood electrical properties for RF applicati..
Shear Strength	28.3 MPa	4100 psi	Overlap, Brass MEK/abrade/MEK
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M
Shear Strength	28.3 MPa	4100 psi	Overlap, Aluminum - abraded, 150 grit sandpaper, Adhesive Failure
3M Scotch-Weld™ DP807 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP807 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact, durability and..
Shear Strength	28.3 MPa	4100 psi	Overlap, Etched Aluminum tested after 1 week of Immersion in IPA
3M Scotch-Weld™ DP807 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP807 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact, durability and..
Shear Strength	28.3 MPa	4100 psi	Overlap, Bare Aluminum, Cohesive Failure
3M Scotch-Weld™ DP810NS Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre..
Shear Strength	28.3 MPa	4100 psi	Overlap, Aluminum, Cohesive Failure
3M Scotch-Weld™ DP8405NS Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP8405NS is a high performance, two-part acrylic adhesives that offer excellent shear, peel and impact performance. These toughened adhesives provide improved adh..
Shear Strength	28.3 MPa	4100 psi	Overlap, Aluminum - bare, Adhesive Failure
3M Scotch-Weld™ DP825 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP825 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact, durability and..
Shear Strength	28.3 MPa	4100 psi	Aluminum, etched, Overlap, 30 day Gasoline soak, Cohesive Failure
3M Scotch-Weld™ LSB60 Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60 is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of f..