Polymer Property : Shear Strength = 3700 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	25.5 MPa	3700 psi	Interlaminar S23; ASTM D2344
Polystrand ThermoPro™ IE6010 Unitape Unidirectional Polypropylene-Glass Composite Fiber Orientation is 0°.Polystrand ThermoPro™ combines continuous E-Glass (ThermoPro-E™) structural reinforcing fibers in either a polyethylene or polypropylene proprietary thermoplastic polymer ..
Shear Strength	25.5 MPa	3700 psi	Tensile
Resin Technology Group Fusion 1 General Purpose Fusion Cyanoacrylate Information provided by Resin Technology Group.
Shear Strength	25.5 MPa	3700 psi	ASTM D732
Spartech Polycast Poly 2000 (Mil-P-25690;Class 1) Cell Cast Acrylic Description: Cell Cast AcrylicInformation provided by Spartech.
Shear Strength	25.5 MPa	3700 psi	ASTM D732
Spartech Polycast Poly 2000 (Mil-P-25690;Class 2) Cell Cast Acrylic Description: Cell Cast AcrylicInformation provided by Spartech.
Shear Strength	25.5 MPa	3700 psi	Overlap at 2 hrs after bonding
3M Scotch-Weld™ DP810NS Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre..
Shear Strength	25.5 MPa	3700 psi	Overlap, Aluminum, Cohesive Failure
3M Scotch-Weld™ DP8810NS Low Odor Acrylic Adhesives 3M™ Scotch-Weld™ Low Odor Acrylic Adhesives are high performance, two-part acrylic adhesives with lower odor than most acrylic adhesives. These toughened products offer excellent shear, peel, and ..
Shear Strength	25.5 MPa	3700 psi	Overlap, Etched Aluminum, 65°C/80% RH for 30 days, Cohesive Failure
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i..
Shear Strength	25.5 MPa @Temperature -55.0 °C	3700 psi @Temperature -67.0 °F	Aluminum, Overlap; ASTM D1002
3M Scotch-Weld™ LSB90 Flexible Epoxy 3M™ Scotch-Weld™ Epoxy Adhesive LSB90 is a high performance, two-part, flexible epoxy adhesive offering high shear and peel adhesion and very high levels of durability. It has a 90 minute worklife..
Shear Strength	25.5 MPa	3700 psi	Overlap, Stainless Steel-MEK/Abrade/MEK, Cohesive/Adhesive Failure
3M Scotch-Weld™ LSB60 Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60 is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of f..