Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 2.41 MPa | 350 psi | Plate Shear, W Direction, typ |
Hexcel® HexWeb® CR III 1/16-5052-.0007 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
Shear Strength | >= 2.41 MPa | >= 350 psi | Plate Shear, L Direction, min |
Hexcel® HexWeb® CR III 1/8-5056-.001 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
Shear Strength | 2.41 MPa | 350 psi | Plate Shear, W Direction, typ |
Hexcel® HexWeb® CR III 3/8-5052-.005 Corrosion Resistant Specification Grade Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge."5052 and 5056 expanded aerospace grade aluminum honeycomb materials are available in a wide selection of cell sizes and foil gauges. The HexWeb CR.. |
|||
Shear Strength | >= 2.41 MPa | >= 350 psi | Plate Shear, L Direction, min |
Hexcel® HexWeb® CR-PAA™ 1/8-5056-0.001 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa.. |
|||
Shear Strength | 2.41 MPa | 350 psi | Plate Shear, W Direction, typ |
Hexcel® HexWeb® CR-PAA™ 3/8-5052-0.005 Phosphoric Acid Anodized Aluminum Honeycomb Grade is designated as "Cell Size-Alloy-Foil Gauge." The life cycle of aluminum honeycomb sandwich structures in a given application can be directly related to the quality of the bond between the fa.. |
|||
Shear Strength | >= 2.41 MPa | >= 350 psi | Plate Shear, W Direction, min |
Hexcel® HexWeb® HRP - 3/8 - 8.0 Fiberglass/Phenolic Honeycomb Designation: Material-Cell Size (inches)-DensityHexWeb HRP is a glass fabric reinforced honeycomb in which a heat-resistant phenolic resin is used both for initial and final impregnations. This prod.. |
|||
Shear Strength | >= 2.41 MPa | >= 350 psi | Plate Shear, W Direction, min |
Hexcel® HexWeb® HRP/OX - 1/4 - 7.0 Fiberglass/Phenolic Honeycomb Designation: Material-Cell Size (inches)-DensityHexWeb HRP is a glass fabric reinforced honeycomb in which a heat-resistant phenolic resin is used both for initial and final impregnations. This prod.. |
|||
Shear Strength | 2.41 MPa | 350 psi | cured 14 days @ 50% RH; AMS3265 |
3M AC-730 Class C-4 (168) Aerospace Sealant 3M Aerospace Sealant AC-730 Class C are two-part, manganese-cured, non-chromate corrosion inhabiting sealants. These Sealants provide an effective barrier against the common causes of corrosion on a.. |
|||
Shear Strength | 2.41 MPa | 350 psi | Lap; ASTM D1002 |
Arlon Thermabond® 99720W015 0.015" Uncured Silicone Rubber with PTFE Coated Fiberglass Carrier Design/Construction:Liner: 0.001" FEP FilmSide 1: Uncured Silicone RubberCarrier: 0.003" PTFE coated FiberglassRecommended Primer: Dow Corning S2260This data represents typical values for the pr.. |
|||
Shear Strength | 2.41 MPa | 350 psi | On Douglas Fir |
3M Scotch-Weld™ 3792LM Low Melt Adhesive Clear multi-purpose for wood, coated paper, polyolefins and other heat-sensitive materials; P.O.P. displays and use with low melt applicator onlyInformation provided by 3M |
|||
Shear Strength | 2.41 MPa | 350 psi | On Douglas Fir |
3M Scotch-Weld™ 3797 Hot Melt Adhesive High ball and ring; Low viscosity and Good for electrical pottingInformation provided by 3M |
|||
Shear Strength | 2.41 MPa | 350 psi | Overlap, Isopropyl Alcohol Wipe surface prep, FRP |
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 2.41 MPa | 350 psi | Overlap, Isopropyl Alcohol Wipe surface prep, Phenolic |
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 2.41 MPa | 350 psi | Overlap, Isopropyl Alcohol/Abrade/Isopropyl Alcohol surface prep, PVC |
3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat.. |
|||
Shear Strength | 2.41 MPa | 350 psi | Overlap, ABS |
3M Scotch-Weld™ DP405 LH Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP405 LH is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive which has a 5 minute work life and accelerated cure. It exhibits excellent shear and peel.. |
|||
Shear Strength | 2.41 MPa | 350 psi | Overlap, Particleboard, Substrate Failure |
3M Scotch-Weld™ Thin Instant Wood Adhesives and Surface Activator 3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in t.. |
|||
Shear Strength | 2.41 MPa | 350 psi | Overlap, Melamine, Substrate Failure |
3M Scotch-Weld™ Thin Instant Wood Adhesives and Surface Activator 3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in t.. |
|||
Shear Strength | 2.41 MPa | 350 psi | cured 14 days @ 50% RH; AMS3265 |
3M AC-730 Class C-8 (24) Aerospace Sealant 3M Aerospace Sealant AC-730 Class C are two-part, manganese-cured, non-chromate corrosion inhabiting sealants. These Sealants provide an effective barrier against the common causes of corrosion on a.. |
|||
Shear Strength | 2.41 MPa | 350 psi | Overlap, Acrylic |
3M Scotch-Weld™ DP190 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP190 Translucent is a 1:1 mix ratio similar to Scotch-Weld™ Epoxy Adhesive 2216 B/A Translucent but faster curing.Information provided by 3M |
|||
Shear Strength | 2.41 MPa | 350 psi | |
Dow Corning 3-0115 AUTOMOTIVE SEALANT One-part, self-priming, noncorrosive, alkoxy-cure, RTV silicone rubber designed for automotive powertrain sealing applicationsInformation provided by Dow Corning |