Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 21.4 MPa | 3100 psi | Tensile lap, Al to Al |
Master Bond EP65ND Fast Curing, High Shear Strength Epoxy This two component adhesive system is formulated to cure quickly at ambient temperatures e.g. 8-10 minutes, shorter lives at higher temperatures for maximum bond strength. Tensile lap shear strength.. |
|||
Shear Strength | 21.4 MPa | 3100 psi | Overlap, Copper (MEK/abrade/MEK), Cohesive failure/Adhesive Failure; ASTM D1002 |
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i.. |
|||
Shear Strength | 21.4 MPa | 3100 psi | Overlap, grit-blasted steel; ASTM D1002 |
3M Scotch-Weld™ MC100 Metal Instant Adhesive 3M™ Scotch-Weld™ Metal Instant Adhesives are designed to give optimum performance and high strength bonds on metals, including galvanized or anodized surfaces. MC100 (formerly SB30 or SB96) is a l.. |
|||
Shear Strength | 21.4 MPa | 3100 psi | Overlap, grit-blasted steel; ASTM D1002 |
3M Scotch-Weld™ MC5 Metal Instant Adhesive 3M™ Scotch-Weld™ Metal Instant Adhesives are designed to give optimum performance and high strength bonds on metals, including galvanized or anodized surfaces. MC5 (formerly SP93) is a very low vi.. |
|||
Shear Strength | 21.4 MPa | 3100 psi | cured, grit-blasted steel; ASTM D1002 |
3M Scotch-Weld™ PR100 Plastic and Rubber Instant Adhesive 3M™ Scotch-Weld™ Plastic and Rubber Instant Adhesive is designed to give exceptional performance on difficult-to-bond plastic and rubber substrates. This adhesive may be bonded to like substrates .. |
|||
Shear Strength | 21.4 MPa | 3100 psi | Overlap, CRS, Cohesive Failure |
3M Scotch-Weld™ DP810 Tan Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 21.4 MPa | 3100 psi | Overlap, Aluminum -120 frit sandpaper |
3M Scotch-Weld™ DP820 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP820 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability .. |
|||
Shear Strength | 21.4 MPa @Temperature -55.0 °C |
3100 psi @Temperature -67.0 °F |
Overlap, Etched Alum/Etched Alum |
3M Scotch-Weld™ DP820 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP820 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability .. |
|||
Shear Strength | 21.4 MPa @Temperature 24.0 °C, Time 1.04e+6 sec |
3100 psi @Temperature 75.2 °F, Time 288 hour |
Overlap, Cured for 7 days at 24°C |
3M Scotch-Weld™ 2216 B/A Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 2216 B/A is a flexible, two-part, room temperature curing epoxy with high peel and shear strength. Scotch-Weld epoxy adhesive 2216 B/A is identical to 3M Scotch-Wel.. |
|||
Shear Strength | 21.4 MPa | 3100 psi | Overlap, Etched Al, Hydrocarbon Fluid for 7 days |
3M Scotch-Weld™ 2216 B/A Tan NS Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 2216 B/A is a flexible, two-part, room temperature curing epoxy with high peel and shear strength. Scotch-Weld epoxy adhesive 2216 B/A is identical to 3M Scotch-Wel.. |
|||
Shear Strength | 21.4 MPa | 3100 psi | Overlap, CRS/CRS; ASTM D1002 |
3M Scotch-Weld™ 2216 B/A Tan NS Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 2216 B/A is a flexible, two-part, room temperature curing epoxy with high peel and shear strength. Scotch-Weld epoxy adhesive 2216 B/A is identical to 3M Scotch-Wel.. |