Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Shear Strength | 27.6 - 41.4 MPa | 4000 - 6000 psi | |
ND Industries High Temperature SuperGlue 311 Very high viscosity with thermal cycling resistance |
|||
Shear Strength | 27.6 MPa | 4000 psi | |
NextGen Adhesives G907-25 Optical Epoxy Adhesive Description: NGAC G907-25 is a low viscosity and clear adhesive system that is specifically formulated for optical and laser applications.Advantages and Applications: The NGAC G907-25 provides high .. |
|||
Shear Strength | 27.6 MPa | 4000 psi | Cured, tensile |
Resin Technology Group CT-988 Cationic UV Cure Epoxy Adhesive CT 988 is an epoxy-based, paste-viscosity, cationic-curable adhesive/sealant. This product is activated by exposure to medium intensity UV radiation resulting in a high strength, chemical resistant,.. |
|||
Shear Strength | 27.6 MPa | 4000 psi | Tensile |
Resin Technology Group Fusion 509 Thixotropic Fusion Cyanoacrylate Information provided by Resin Technology Group. |
|||
Shear Strength | >= 27.6 MPa | >= 4000 psi | 2 hours, 65°C |
Resin Technology Group TIGA 202-EX High Performance, Fast Cure Adhesive Mix ratio 2 to 1 by volume.TIGA 202-EX is a two-part epoxy adhesive offering outstanding shear tensile and peel adhesion. TIGA 202-EX offers a 20 minute pot life and good hardness development within.. |
|||
Shear Strength | 27.6 MPa | 4000 psi | |
Resinlab® RC8048 Anaerobic Retaining Compound The RC 8000 Series anaerobic retaining compounds are designed for use in demanding applications to fill the spaces and surface irregularities between tightly mated cylindrical parts. These products .. |
|||
Shear Strength | >= 27.6 MPa | >= 4000 psi | 2 hours, 65°C |
Resin Technology Group TIGA 216-EX High Performance Adhesive Mix ratio 2 to 1 by volume.TIGA 216-EX is a two-part epoxy adhesive offering outstanding shear tensile and peel adhesion. TIGA 216-EX offers a 60 minute pot life and good hardness development within.. |
|||
Shear Strength | 27.6 - 34.5 MPa | 4000 - 5000 psi | ASTM D732 |
Mar-Bal MB2000-5 Thermoset Polyester Composite Molding Compound An excellent flame and track resistant material with excellent electrical and mechanical properties. Good dielectric strength and low shrink for close dimensional control.Mar-Bal standard grades can.. |
|||
Shear Strength | 27.6 - 34.5 MPa | 4000 - 5000 psi | ASTM D732 |
Mar-Bal MB2000-8 Thermoset Polyester Composite Molding Compound An excellent flame and track resistant material with excellent electrical and mechanical properties. Good dielectric strength and low shrink for close dimensional control.Mar-Bal standard grades can.. |
|||
Shear Strength | 27.6 MPa | 4000 psi | |
Indium Corp. Indalloy 141 Tin-Lead Solder Alloy Information Provided by Indium Corporation |
|||
Shear Strength | 27.6 MPa | 4000 psi | Short Beam |
COI Ceramics Sylramic™ S400 Silicon Carbide Ceramic Matrix Composite, Carbon Description: Engineered ceramic composite structures for a broad range of industries and applications.Reinforcing Fiber Flexibility: S400 - Carbon Preceramic Polymer Matrix Precursors: S400 - Crysta.. |
|||
Shear Strength | 27.6 MPa | 4000 psi | Overlap, CRS Oakite degrease |
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 27.6 MPa | 4000 psi | Overlap, Copper MEK/abrade/MEK |
3M Scotch-Weld™ DP420 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 27.6 MPa | 4000 psi | Overlap, Copper MEK/abrade/MEK |
3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat.. |
|||
Shear Strength | 27.6 MPa | 4000 psi | Overlap, Brass CDA 260 |
3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat.. |
|||
Shear Strength | 27.6 MPa | 4000 psi | Overlap, Stainless Steel MEK/abrade/MEK |
3M Scotch-Weld™ DP460 Off-White Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP460 Off-White and DP460 NS are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion and very high levels of durability.Informat.. |
|||
Shear Strength | 27.6 MPa | 4000 psi | Overlap, 50% Antifreeze for 14 days, Cohesive Failure |
3M Scotch-Weld™ DP810NS Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 27.6 MPa | 4000 psi | Overlap at 2 hrs after bonding |
3M Scotch-Weld™ DP810NS Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 27.6 MPa @Temperature 24.0 °C |
4000 psi @Temperature 75.2 °F |
Overlap |
3M Scotch-Weld™ DP810NS Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre.. |
|||
Shear Strength | 27.6 MPa | 4000 psi | Overlap, Etched Aluminum, Isopropanol at RT for 30 days immersion, Cohesive Failure |
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i.. |
|||
Shear Strength | 27.6 MPa | 4000 psi | Overlap, Aluminum-etched, Cohesive failure; ASTM D1002 |
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i.. |
|||
Shear Strength | 27.6 MPa @Temperature 23.0 °C |
4000 psi @Temperature 73.4 °F |
Overlap, Aluminum |
3M Scotch-Weld™ DP920 Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP920 is a two-part, 2:1 mix ratio, toughened epoxy structural adhesive with a 20 minute work life. It exhibits excellent shear and peel strengths along with good i.. |
|||
Shear Strength | 27.6 MPa | 4000 psi | Aluminum, etched, Overlap, 30 day Gasoline soak, Cohesive Failure |
3M Scotch-Weld™ LSB60NS Toughened Epoxy Adhesives 3M™ Scotch-Weld™ Toughened Epoxy Adhesive LBS60NS is a high performance, two-part, toughened epoxy adhesives offering outstanding shear adhesion and very high levels of durability with a choice of.. |
|||
Shear Strength | 27.6 MPa @Temperature -55.0 °C |
4000 psi @Temperature -67.0 °F |
Overlap |
3M Scotch-Weld™ DP125 Translucent Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive DP125 Translucent is a faster curing version of 3M Scotch-Weld Epoxy Adhesive 2216 Translucent B/A. The worklife and cure time has been reduced from hours and days .. |
|||
Shear Strength | 27.6 MPa | 4000 psi | Overlap, Aluminum Oakite degrease |
3M Scotch-Weld™ DP420 Black Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 27.6 MPa | 4000 psi | Overlap, Water Vapor, 49°C at 100% RH for 30 days |
3M Scotch-Weld™ DP420 Black Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 27.6 MPa | 4000 psi | Overlap, Water Vapor, 93°C at 100% RH for 14 days |
3M Scotch-Weld™ DP420 Black Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 27.6 MPa | 4000 psi | Overlap, Skydrol LD-4 immersion, 66°C for 30 days |
3M Scotch-Weld™ DP420 Black Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive are high performance, two-part epoxy adhesives offering outstanding shear and peel adhesion, and very high levels of durability.Information provided by 3M |
|||
Shear Strength | 27.6 MPa | 4000 psi | |
Resinlab® RC8020 Anaerobic Retaining Compound The RC 8000 Series anaerobic retaining compounds are designed for use in demanding applications to fill the spaces and surface irregularities between tightly mated cylindrical parts. These products .. |