Polymer Property : Shear Strength = 1900 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Shear Strength	13.1 MPa	1900 psi	Cured 60 minutes at 125°C, Alum/Alum
Resin Technology Group TIGA 901 Room Temperature Curing Silver Conductive Epoxy 100 parts resin to 6 parts hardener. Cure 24 hours at 25°C, 1-4 hours at 65°C, 30-60 minutes at 125°C, or 30 minutes at 150°C.TIGA 901 is an electrically conductive, silver filled epoxy adhesiv..
Shear Strength	13.1 MPa	1900 psi	Cured 2 hours at 125°C, Al/Al
Resin Technology Group TIGA 908 Gold Bonder - Low Stress Silver Conductive 100 parts resin to 6 parts hardener.TIGA 908 is a low stress, conductive silver filled epoxy adhesive. It is recommended for bonding, and sealing electronic applications which require bonding to gol..
Shear Strength	13.1 MPa	1900 psi	Bond, Al to Al, after 30 days water immersion
Master Bond EP34AO Epoxy Compound Withstands High Temperatures Description: Master Bond Polymer System EP34AO is a room temperature curing, two component epoxy compound for high temperature bonding and sealing applications especially where thermal conductivity ..
Shear Strength	13.1 MPa	1900 psi	Long Beam Shear, L Direction
Hexcel® HexWeb® HDC - 3/16 - 16.0 (R2) Heavy Density Core Designation: Material-Cell Size (inches)-DensityHexWeb® HDC is a fabric reinforced honeycomb, typically made from either fiberglass or carbon prepreg. A thermosetting node adhesive is used with eit..
Shear Strength	13.1 MPa	1900 psi	Overlap, Cold Rolled Steel
3M Scotch-Weld™ DP125 Gray Epoxy Adhesive Scotch-Weld epoxy adhesive DP125 Gray is a filled, pigmented version of the Scotch-Weld epoxy adhesive DP125 Translucent and has similar performance and flexibility properties.Information provided b..
Shear Strength	13.1 MPa	1900 psi	Overlap, PVC, Substrate Failure
3M Scotch-Weld™ DP8005 Black Structural Adhesive 3M™ Scotch-Weld™ Structural Plastic Adhesive DP-8005 is a two-part acrylic-based adhesive (10:1 ratio by volume) that can bond many low surface energy plastics, including many grades of polypropyl..
Shear Strength	13.1 MPa	1900 psi	Overlap, Green FRP, Cohesive Failure
3M Scotch-Weld™ DP810NS Structural Adhesive 3M™ Scotch-Weld™ Low-Odor Acrylic Adhesives are two-part, 1:1 mix ratio, toughened structural adhesives with less odor than most acrylic adhesives. The adhesives have excellent shear and peel stre..
Shear Strength	13.1 MPa	1900 psi	Overlap, PVC, Substrate Failure
3M Scotch-Weld™ DP8405NS Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP8405NS is a high performance, two-part acrylic adhesives that offer excellent shear, peel and impact performance. These toughened adhesives provide improved adh..
Shear Strength	13.1 MPa @Temperature 66.0 °C	1900 psi @Temperature 151 °F	Overlap, Oak, Substrate/Adhesive Failure
3M Scotch-Weld™ Thick Instant Wood Adhesives and Surface Activator 3M™ Scotch-Weld™ Instant Wood Adhesives an Surface Activator are single component, room temperature-curing adhesives that provides cure and speed and shear strength for demanding applications in t..
Shear Strength	13.1 MPa @Temperature 83.0 °C	1900 psi @Temperature 181 °F	Overlap, Etched Alum/Etched Alum
3M Scotch-Weld™ DP820 Acrylic Adhesives 3M™ Scotch-Weld™ Acrylic Adhesive DP820 is a two-part, 1:1 mix ratio, toughened acrylic structural adhesives. They exhibit excellent shear and peel strengths along with good impact and durability ..
Shear Strength	13.1 MPa	1900 psi	Overlap, Stainless Steel/Stainless Steel; ASTM D1002
3M Scotch-Weld™ 2216 B/A Gray Epoxy Adhesive 3M™ Scotch-Weld™ Epoxy Adhesive 2216 B/A is a flexible, two-part, room temperature curing epoxy with high peel and shear strength. Scotch-Weld epoxy adhesive 2216 B/A is identical to 3M Scotch-Wel..