Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Dart Drop | 7.88 g/micron | 200 g/mil | ASTM D1709A |
Westlake Mxsite LC78105-C Polyethylene Film, Using Energx Technology Services
(discontinued **) Mxsite LC78105-C polyethylene is recommended for the skin layers of blown stretch film. It will provide a very aggressive cling force in both a stretched and unstretched condition. The excellent cli.. |
|||
Dart Drop | 7.87 g/micron | 200 g/mil | F50; ASTM D1709 |
ExxonMobil Escorene® LD-333 EVA Film Resin, Very High Clarity, Very High Impact
(discontinued **) Data provided by the manufacturer, Exxon Chemical.A 9.0% vinyl acetate copolymer film resin. Film made from LD-333 exhibits superior impact strength, clarity and heat sealability.Applications: Prim.. |
|||
Dart Drop | 7.87 g/micron | 200 g/mil | ASTM D1709 |
Huntsman PE1503 EVA Film Extrusion
(discontinued **) 5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi.. |
|||
Dart Drop | 7.87 g/micron | 200 g/mil | ASTM D1709 |
Huntsman PE1504 EVA Film Extrusion
(discontinued **) 5% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi.. |
|||
Dart Drop | 7.87 g/micron | 200 g/mil | ASTM D1709 |
Huntsman PE1605 EVA Film Extrusion
(discontinued **) 6% Vinyl Acetate EVA copolymer and FDA compliantFeatures: Excellent balance of optical and strength, toughness and flexibility at low temperatures, and good heat seal characteristic.Applications: Fi.. |
|||
Dart Drop | 7.87 g/micron | 200 g/mil | ASTM D1709 |
Huntsman Rexell® L8102 Cast Film Extrusion LLDPE
(discontinued **) Linear-low density copolymer with high slip and medium antiblock, general purpose blown film extrusion, FDA compliant.Features: Excellent combination of sealability, mechanical strength and optics.A.. |