Polymer Property : Tensile Strength, Ultimate = 9860 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ASTM D638
Plaskolite Optix® CA-71 General Purpose Acrylic Resin
Injection Molding and Extrusion Grade Pellets. High heat resistance, medium flow.
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ASTM D638
Plaskolite Optix® CA-82 General Purpose Acrylic Resin
Injection Molding Grade Pellets. Highest Molecular Weight, good heat resistance. Superior mold release.
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ASTM D638
Plaskolite West Optix® CA-82 General Purpose Acrylic Resin
Injection Molding Grade Pellets. Highest Molecular Weight, good heat resistance. Superior mold release.
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ASTM D638
Plaskolite West Optix® CA-71 General Purpose Acrylic Resin
Injection Molding and Extrusion Grade Pellets. High heat resistance, medium flow.
Tensile Strength, Ultimate 68.0 - 250 MPa
9860 - 36300 psi
Average value: 143 MPa Grade Count:110
Overview of materials for Nylon 66, Glass Fiber/PTFE Filled
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass Fiber/PTFE Filled". Each property range of values reported is minimum and maximum values..
Tensile Strength, Ultimate 68.0 MPa
9860 psi
5 mm/min; ISO 527
Lucite International Perspexâ„¢ XT IM50 Acrylic Extruded Sheet
PERSPEX extruded sheet has a lower molecular weight making it easy to vacuum form and the extrusion process gives excellent thickness tolerance and is economical for long production runs.Information..
Tensile Strength, Ultimate 68.0 MPa

@Temperature 1093 °C
9860 psi

@Temperature 1999 °F
Haynes HR-160® alloy, solution annealed sheet
Outstanding resistance to various forms of high-temperature corrosion attack, excellent resistance to sulfidation and chloride attack in both reducing and oxidizing atmospheres. Excellent forming an..
Tensile Strength, Ultimate 68.0 MPa
9860 psi
DIN 53504
Lubrizol ESTANE® 5722 Ester Based Thermoplastic Polyurethane (European Grade)
Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability ..
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ASTM D638-10
DSM Somos® PerFORM Stereolithography Polymer, UV Postcure
PerFORM produces strong, stiff, high-temperature resistant composite parts on standard 355 nm stereolithography machines. This material’s lower viscosity makes processing parts faster. It exhibits ..
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ATSM D638
Ashley Polymers Ashlene® 526LD Nylon 66
Modified for toughness at low temperatures, injection molding grade.Data provided by the manufacturer
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ATSM D638
Ashley Polymers Ashlene® 528BR-WO Nylon 66
A rust colored flame retardant Nylon 66 with a UL 94 V-0 rating.Data provided by the manufacturer
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ATSM D638
Ashley Polymers Ashlene® 291WO PPO
A reinforced, flame retardant resin with outstanding structural strength. Good appearance and high impact.Data provided by the manufacturer
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ATSM D638
Ashley Polymers Ashlene® 526 Nylon 66
High impact Nylon 66 with good stiffness and good low temperature properties for injection molding. Values shown are for Natural. Colors may change some properties.Data provided by the manufacture..
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ASTM D638
A. Schulman ComAlloy Hiloy® 212 Polystyrene, Glass Reinforced
Data provided by the manufacturer, ComAlloy International Company.20% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ASTM D638
A. Schulman ComAlloy Hiloy® 636 Nylon 6/6, Glass/Mineral Reinforced, Flow Enhanced
Data provided by the manufacturer, ComAlloy International Company.40% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ASTM D638
A. Schulman ComAlloy Voloy® 113 Polypropylene, Glass Reinforced, Chemically Coupled, Flame Retardant, UL
Data provided by the manufacturer, ComAlloy International Company.25% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ASTM D638
Asahi Kasei Delpet® 560F Acrylic Molding Compound
560F has the highest flow of Delpet® grades, allowing reduced screw load for broad selection of molding conditions. General Delpet® qualities include attractive transparency, elegant luster and c..
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ISO 527-1, 2
Polyplastics Duracon® HP25X Acetal Co-polymer (POM), High stiffness, High viscosity
DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..
Tensile Strength, Ultimate 68.0 MPa
9860 psi
ISO 527-1, 2
Polyplastics Duracon® HP90X Acetal Co-polymer (POM), High stiffness, General
DURACON® is a crystalline thermoplastic acetal copolymer. The primary raw material trioxane, a trimer of formaldehyde.The thermoplastic adopts a copolymer structure in which polyoxymethylene (-C-O)..