Polymer Property : Tensile Strength, Ultimate = 95.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 95.0 - 262 MPa
13800 - 38000 psi
Average value: 177 MPa Grade Count:16
Overview of materials for Polyaryletherketone (PAEK), Carbon Fiber Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polyaryletherketone (PAEK), Carbon Fiber Filled". Each property range of values reported is minimum and ..
Tensile Strength, Ultimate 95.0 MPa
13800 psi
ASTM D638
Shell Carilon® DB6F1G30 Polyketone, Flame-Retarded, Tracking-Resistant, Glass-Reinforced Injection Molding Grade &n
Shell announced in Feb. 2000 that the Carilon product line is being discontinued. CARILON Polymer DB6F1G30 is a flame-retarded, 15 percent glass-fiber-reinforced, injection molding grade with mecha..
Tensile Strength, Ultimate 95.0 MPa
13800 psi
ISO 527
Wellman Wellamid® GFT15N050-N2 15% Impact Modified Glass Reinforced Nylon 66/6, Lubricated & Heat Stabilized &n
Typical Applications: Machinery gear trains and linkage, conveyor belt links, fasteners, auto under hood and door parts, automotive door handles, appliance parts, sporting goods, lawn and garden equ..
Tensile Strength, Ultimate 95.0 - 173.058 MPa

@Temperature -40.0 - 120 °C
13800 - 25100.0 psi

@Temperature -40.0 - 248 °F
Average value: 125 MPa Grade Count:2
Overview of materials for Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler". Specific grades with glass content between 25%..
Tensile Strength, Ultimate 95.0 MPa

@Temperature 1095 °C
13800 psi

@Temperature 2003 °F
Haynes 625 alloy, cold rolled and 1050°C mill-annealed sheet
Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of ..
Tensile Strength, Ultimate 95.0 MPa
13800 psi
ISO 527-93
Wellman Wellpet® MRGF101-GY1 PET, 29% Mineral/Glass Fiber Reinforced
Typical data obtained from injection molded test bars, tested dry as molded at 73°F (23°C). Information provided by Wellman, Inc. Engineering Resins Division.
Tensile Strength, Ultimate 95.0 MPa

@Temperature 180 °C
13800 psi

@Temperature 356 °F
ISO 527-1/-2
DSM Stanyl® 46HF4530 PA46-GF30
30% Glass Reinforced, Heat Stabilized, High Flow, for E&E applications
Tensile Strength, Ultimate 95.0 MPa

@Temperature 180 °C
13800 psi

@Temperature 356 °F
ISO 527-1/-2
DSM Stanyl® TW200B6 PA46-CF30
30% Carbon Reinforced, Heat Stabilized, Lubricated
Tensile Strength, Ultimate 95.0 MPa

@Temperature 200 °C
13800 psi

@Temperature 392 °F
ISO 527-1/-2
DSM Stanyl® TW271B6 (PA46+PTFE)-CF30
30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified
Tensile Strength, Ultimate 95.0 MPa
13800 psi
dry; ISO 527-1/-2
DSM EcoPaXX® Q-HGM24 PA410-(GF+MD)30
10% Glass Reinforced, 20% Mineral Reinforced, Heat Stabilized
Tensile Strength, Ultimate 95.0 MPa
13800 psi
dry; ISO 527-1/-2
DSM EcoPaXX® Q-HXGM24 PA410-(GF+MD)30
% Glass Reinforced, % Mineral Reinforced, Heat Stabilized
Tensile Strength, Ultimate 95.0 MPa
13800 psi
ATSM D638
Ashley Polymers Ashlene® P265 PPO, 20% Glass Reinforced
A general purpose, 20% glass reinforced PPO resin for injection molding applications requiring structural strength, dimensional stability and good heat resistance.Data provided by the manufacturer
Tensile Strength, Ultimate 95.0 MPa
13800 psi
ATSM D638
Ashley Polymers Ashlene® P265WO PPO, 20% Glass Reinforced
A general purpose, 20% glass reinforced flame retardant, PPO resin for injection molding applications requiring structural strength, dimensional stability and good heat resistance.Data provided by t..
Tensile Strength, Ultimate 95.0 MPa
13800 psi
ASTM D638
A. Schulman ComAlloy Hiloy® 130 Polypropylene, Glass/Mineral Reinforced, Chemically Coupled, UL
Data provided by the manufacturer, ComAlloy International Company.40% Glass/Mineral Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 95.0 MPa
13800 psi
ASTM D638
A. Schulman ComAlloy Voloy® 688 Nylon 6/6, Glass Fiber/Bead Reinforced, Nylon 6/6 Alloy, Flame Retardant, UL
Data provided by the manufacturer, ComAlloy International Company.45% Glass Fiber/Bead Reinforced. Halogen- and phosphorous-freeThe ComAlloy product line has been integrated into the A Schulman prod..
Tensile Strength, Ultimate 95.0 MPa
13800 psi
ISO 527
LATI LARTON GCE/60 60% Mixed Glass Fiber and Special Mineral Filled Polyphenylene sulfide (PPS)  (discontinued
Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex..
Tensile Strength, Ultimate 95.0 MPa

@Temperature 120 °C
13800 psi

@Temperature 248 °F
ISO 527
LATI LARTON G/30 30% Glass Fiber Filled Polyphenylene sulfide (PPS)  (discontinued **)
Description: Larton thermoplastics are polyphenylene sulfide (PPS) products. They are distinguished by a group of very interesting properties combined with easy moldability. Larton parts feature: ex..
Tensile Strength, Ultimate 95.0 MPa

@Temperature 180 °C
13800 psi

@Temperature 356 °F
ISO 527-1/-2
DSM Stanyl® TS200F6 PA46-GF30
30% Glass Reinforced