Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 6.21 MPa | 900 psi | |
Sylvin Technologies 9077-80 LMW Natural PVC for Injection Molding Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 6.21 MPa | 900 psi | |
Dow Corning SILASTIC® 25787 SILICONE RUBBER NATURAL Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 6.21 MPa | 900 psi | |
Dow Corning SILASTIC® J RTV SILICONE RUBBER BASE & CURING AGENT High durometer silicone mold making rubber recommended for use with rigid and foam polyurethane and can be used with polyesters and epoxies.Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 6.21 MPa | 900 psi | ASTM D638 |
Dow AFFINITY™ EG 8200G Ethylene alpha-olefin copolymer AFFINITY™ EG 8200G Polyolefin Plastomer (POP) is produced via INSITE™ Technology from Dow Plastics. It exhibits high flexibility and elasticity. It can be utilized in monolayer cast film and in .. |
|||
Tensile Strength, Ultimate | 6.21 MPa | 900 psi | |
Dow Corning 5-8601 FLUOROSILICONE LSR, KIT Fluorosilicone rubber designed for liquid injection moldingInformation provided by Dow Corning |
|||
Tensile Strength, Ultimate | 6.21 MPa | 900 psi | Bond strength to metal |
Dymax Light Weld® 401 High Clarity Glass Bonding Adhesive Glass Bonding in SecondsDescriptionDymax Light Weld® 400 Series adhesives form high-clarity, invisible bonds between glass and other substrates in seconds. In addition to many structural glass bond.. |
|||
Tensile Strength, Ultimate | 6.21 MPa | 900 psi | silicone property; ASTM D412 |
Arlon I51576R015 Silicone Rubber/Fiberglass/Alloy Laminate Top layer of side 2: alloy 600 foil; Bottom layer of side 2: cured silicone rubber; Substrate is 7628 fiberglass; Side 1: cured silicone rubber |
|||
Tensile Strength, Ultimate | 6.21 MPa | 900 psi | silicone property; ASTM D412 |
Arlon 53423R032 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil PE; Side 1: cured silicone rubber; Substrate: 2523 fiberglass; Side 2: cured silicone rubber |
|||
Tensile Strength, Ultimate | 6.21 MPa | 900 psi | |
Dow Corning 3120 RTV SILICONE RUBBER Two-part, red, condensation cure, moderate flow, high temperature performance, UL HB, cure speed varied by catalyst type and mix ratio.Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 6.21 - 37.0 MPa | 900 - 5370 psi | Average value: 23.9 MPa Grade Count:23 |
Overview of materials for Polypropylene Glass Bead Filled This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene Glass Bead Filled". Each property range of values reported is minimum and maximum values o.. |