Polymer Property : Tensile Strength, Ultimate = 9.50 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	9.50 MPa	1380 psi	ASTM D638
ExxonMobil Escorene® LD-421 LDPE Power Cable Insulation (discontinued **) Data provided by the manufacturer, Exxon Chemical.A crosslinkable polyethylene homopolymer designed as an electrical grade base resin.Applications: A base resin for fully formulated crosslinkable me..
Tensile Strength, Ultimate	9.50 MPa	1380 psi	500 mm/min (20 in./min.); ASTM D638, Type IV Specimen
Eastman M30036-P Polyethylene (discontinued **) M30036-P is an extrusion coating performance polymer suggested for applications requiring performance similar to LLDPE. Compared to low density coating resins, M30036-P offers superior heat seal st..
Tensile Strength, Ultimate	9.50 MPa	1380 psi	ASTM D638
ITW Plexus Plexusâ„¢ AO420FS Methacrylate Adhesive Two-part adhesive designed for structural bonding of thermoplastic, metal, and composite assemblies.
Tensile Strength, Ultimate	9.50 MPa	1380 psi	at max load; ISO 527
A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy DescriptionFormion® FI 241E is a patented non-reinforced, extrusion grade Ionomer alloy. It has bee formulated for high durability, low gloss, and low temperature ductility.ApplicationFormion® FI..
Tensile Strength, Ultimate	9.50 MPa	1380 psi	at max load; ISO 527
A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy DescriptionFormion® FI 241E is a patented non-reinforced, extrusion grade Ionomer alloy. It has bee formulated for high durability, low gloss, and low temperature ductility.ApplicationFormion® FI..
Tensile Strength, Ultimate	9.50 MPa	1380 psi	at max load; ISO 527
A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy DescriptionFormion® FI 241E is a patented non-reinforced, extrusion grade Ionomer alloy. It has bee formulated for high durability, low gloss, and low temperature ductility.ApplicationFormion® FI..
Tensile Strength, Ultimate	9.50 MPa	1380 psi	at max load; ISO 527
A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy DescriptionFormion® FI 241E is a patented non-reinforced, extrusion grade Ionomer alloy. It has bee formulated for high durability, low gloss, and low temperature ductility.ApplicationFormion® FI..
Tensile Strength, Ultimate	9.50 MPa	1380 psi	at max load; ISO 527
A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy DescriptionFormion® FI 241E is a patented non-reinforced, extrusion grade Ionomer alloy. It has bee formulated for high durability, low gloss, and low temperature ductility.ApplicationFormion® FI..
Tensile Strength, Ultimate	9.50 MPa	1380 psi	at max load; ISO 527
A. Schulman FORMION™ FI 241E Non-Reinforced, Extrusion Grade Ionomer Alloy DescriptionFormion® FI 241E is a patented non-reinforced, extrusion grade Ionomer alloy. It has bee formulated for high durability, low gloss, and low temperature ductility.ApplicationFormion® FI..
Tensile Strength, Ultimate	9.50 MPa	1380 psi	Vulcanizate, Press cured, TC95 +3min at 160°C
Dow Nordel® IP 4520 General Purpose Compound FormulationNordel® IP 4520
Tensile Strength, Ultimate	9.50 MPa	1380 psi	Vulcanizate, Press cured, TC95 +3min at 160°C
Dow Nordel® IP 5565 General Purpose Molding FormulationNordel® IP 5565