Polymer Property : Tensile Strength, Ultimate = 86.0 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 86.0 - 130 MPa
12500 - 18900 psi
Average value: 111 MPa Grade Count:16
Overview of materials for Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polyphenylene Sulfide (PPS) with 20% Glass Fiber Filler". Specific grades with glass content between 15%..
Tensile Strength, Ultimate 86.0 MPa

@Temperature 22.0 °C
12500 psi

@Temperature 71.6 °F
25mm flat samples, compression moulded; ISO 527-4
Menzolit Menzolit® SMC 0390 Unsaturated Polyester UP
SMC 0390 is a standard low profile SMC. Because of its low shrinkage, the material shows good surface quality as well as very low warpage. The product is suitable for applications if a better surfac..
Tensile Strength, Ultimate 86.0 MPa
12500 psi
ASTM D638
Glastic Laminates/Shapes SG-200 High Strength/High Temperature Polyester Laminate
Data provided by Glastic Corporation.NEMA GPO-1. A superior replacement for epoxy-bonded mica in layer insulation applications.
Tensile Strength, Ultimate 86.0 MPa
12500 psi
ASTM D638
Saint-Gobain Meldin® 7001 Isostatically Molded Polyimide
Finished parts and basic shapes made from unfilled polyimide material for structural applications requiring requiring high electrical insulative properties, high purity and low outgassing, and high ..
Tensile Strength, Ultimate 86.0 MPa
12500 psi
ISO 527-1, 2
Polyplastics Duranex® 7195W Polybutylene Terephthalate (PBT), Super low warpage, GF filled
DURANEX® is a crystalline thermoplastic based on polybutylene terephthalate (PBT) that can be readily strengthened, modified, or otherwise performance enhanced through the addition of glass fibers ..
Tensile Strength, Ultimate 86.0 MPa
12500 psi
ASTM Data
Dow Retain® 8209 ABS + Polycarbonate
Data provided by Dow Chemical.
Tensile Strength, Ultimate 86.0 MPa
12500 psi
5mm/min; ISO 527
BASF Ultramid® 7423-2 NF3001 13% Glass Filled PA66 (Conditioned)
Ultramid 7423-2 NF3001 is an impact modified, 13% glass reinforced, heat stabilized injection molding PA6/6.
Tensile Strength, Ultimate 86.0 MPa
12500 psi
ATSM D638
Ashley Polymers Ashlene® P123 PBT Polyester, 15% Glass Reinforced
PBT polyester with 15% glass reinforcement.Data provided by the manufacturer
Tensile Strength, Ultimate 86.0 MPa
12500 psi
ATSM D638
Ashley Polymers Ashlene® P284 PPE Alloy, 10% Glass Reinforced
A 10% glass reinforced PPE Alloy for superior properties and chemical resistance with high heat resistance.Data provided by the manufacturer
Tensile Strength, Ultimate 86.0 MPa
12500 psi
ASTM D638
Chem Polymer Chemlon 109-18 G Nylon 66, 18% Glass Fiber Reinforced
A highly toughened 18% glass fiber reinforced nylon 66 developed for applications requiring stiffness, creep resistance and impact resistance.Data provided by the manufacturer, Chem Polymer.
Tensile Strength, Ultimate 86.0 MPa
12500 psi
ASTM D638
Chem Polymer Durlex 715 G PBT, 15% Glass Reinforced
A lubricated, 15% glass reinforced PBT offering a balance of rigidity, dimensional stability and toughness.Data provided by the manufacturer, Chem Polymer.
Tensile Strength, Ultimate 86.0 MPa
12500 psi
ASTM D638
A. Schulman ComAlloy Comtuf® 635 Nylon 6/6, Glass/Mineral Reinforced, Impact Modified, Flow Enhanced
Data provided by the manufacturer, ComAlloy International Company.40% Glass/Mineral Reinforced. Superior toughness and impact resistance characterize Comtuf® materialsThe ComAlloy product line has ..
Tensile Strength, Ultimate 86.0 MPa
12500 psi
ASTM D638
Chem Polymer Chemlon 223 Nylon 6, Nucleated
A highly nucleated, lubricated nylon 6 intended for applications requiring a faster cycle time. It has increased tensile strength, rigidity, creep resistance and hardness over general purpose nylon..
Tensile Strength, Ultimate 86.0 MPa
12500 psi
ISO value at 5mm/min.
BASF Capron® 8333G Impact Modified, 33% Glass-Filled Nylon 6 (Conditioned)  (discontinued **)
Capron 8333G is a 33% glass reinforced nylon 6 modified compound developed for applications requiring improved dry as molded toughness in combination with a balance of strength, stiffness, and excel..