Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 8.89 MPa | 1290 psi | post cured- 8 hours at 177°C; ASTM D412 |
Multibase C6-515 Dow-Corning Class VI Elastomer Information provided by Multibase |
|||
Tensile Strength, Ultimate | 8.89 MPa | 1290 psi | |
Dow Corning C6-540 LIQUID SILICONE RUBBER KIT Dow Corning® Class VI Elastomers are heat cured elastomer raw materials for use by customers fabricating medical devices and parts.Information provided by Dow Corning |
|||
Tensile Strength, Ultimate | 8.89 MPa | 1290 psi | Silicone Property; ASTM D412 |
Arlon 18976XA023 Silicone Rubber/Fiberglass Laminate Side 1:cured silicone rubber; Substrate: 11523 fiberglass; Side 2: uncured silicone rubber; Interleave: 3 mil Polyethylene |
|||
Tensile Strength, Ultimate | 8.89 MPa | 1290 psi | Silicone Property; ASTM D412 |
Arlon 31970XA015 Silicone Rubber Laminate The interleave is 3 mil of polyethylene, side 1 is uncured silicone rubber and the carrier is HDPE. |
|||
Tensile Strength, Ultimate | 8.89 MPa | 1290 psi | silicone property; ASTM D412 |
Arlon 51976XA015 Silicone Rubber/Fiberglass Laminate Side 1: cured silicone rubber; Substrate: 7628 fiberglass; Side 2: uncured silicone rubber; Interleave: 3 mil polyethylene |
|||
Tensile Strength, Ultimate | 8.89 MPa | 1290 psi | silicone property; ASTM D412 |
Arlon 56976B026 Silicone Rubber/Fiberglass Laminate Side 1: cured silicone rubber; Substrate: 1564 fiberglass; Side 2: uncured silicone rubber; Interleave: 3 mil polyethylene |
|||
Tensile Strength, Ultimate | 8.89 MPa | 1290 psi | silicone property; ASTM D412 |
Arlon 56976XA026 Silicone Rubber/Fiberglass Laminate Interleave: 3 mil PE; Side 1: cured silicone rubber; Substrate: 1564 fiberglass; Side 2: uncured silicone rubber |