Polymer Property : Tensile Strength, Ultimate = 7.60 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	7.60 MPa	1100 psi	ASTM D412
Multibase Multi-Flex® TPE A 7204 LC BLK Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	7.60 MPa	1100 psi	ASTM D412
Multibase Multi-Flex® TPE A 7318 BLK The burn rate is 1 in/min (25 mm/min) based on ASTM FM VSS 302. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	7.60 MPa	1100 psi	ASTM D412
Multibase Multi-Flex® TPE A 8615 BLK This material is currently used in caster wheels where higher abrasion resistance is required. Multi-Flex TPE contains Kraton™ G.Data provided by Multibase.
Tensile Strength, Ultimate	7.60 - 31.0 MPa	1100 - 4500 psi	Average value: 17.1 MPa Grade Count:30
Overview of materials for Methacrylate Adhesive This property data is a summary of similar materials in the MatWeb database for the category "Methacrylate Adhesive". Each property range of values reported is minimum and maximum values of appropri..
Tensile Strength, Ultimate	7.60 MPa	1100 psi	ASTM D638
ExxonMobil Escorene® LD-723 High EVA Extrusion Coating Resin (discontinued **) Data provided by the manufacturer, Exxon Chemical.A high vinyl acetate extrusion coating resin which provides outstanding heat sealability and high clarity. It has a good balance of drawability and..
Tensile Strength, Ultimate	7.60 MPa	1100 psi
Freudenberg Simrit F40 Fluorosilicone Elastomer Combines excellent low-temperature performance of silicone with improved chemical resistance. Very good resistance to military and aerospace fuels. Excellent performance in oxygen plasma environment..
Tensile Strength, Ultimate	7.60 MPa	1100 psi	ASTM D3574E
Mearthane Durethaneâ„¢ M DM-715A Foam Polyurethane MDI backbone: ether.Shore 00 Hardness: 60Summary: Durethane M is a flexible, microcellular, open cell and closed cell urethane foam. Because it is mechanically mixed, the cell size is uniform. Dur..
Tensile Strength, Ultimate	7.60 MPa	1100 psi	Bond Strength Tensile Shear, to ABS or polycarbonate; ASTM D1002
ITW Plexus Plexusâ„¢ MA200 Methacrylate Adhesive Two component adhesive that expands to twice original volume without toxic blowing agents. Used where weight, gap-filling, or increased toughness (vibration damping) is requires for the bonded join..
Tensile Strength, Ultimate	7.60 MPa	1100 psi	Vulcanizate, Press cured, TC95 +3min at 160°C
Dow Nordel® IP 4520 General Purpose Molding FormulationNordel® IP 4520