Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
Hogen Duralloy H100M Molybdenum RWMA Class 13.Typical Resistance Welding Applications: H100M is not as hard as H100W (pure tungsten) and can be drilled or machined to fit parts to be joined. It may be used much the same as H100W .. |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
Kennametal Stellite Deloro® 208 PM after P/M Processing Adhesive wear test data: cast 0.06 Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, s.. |
|||
Tensile Strength, Ultimate | 690 MPa @Temperature 649 °C |
100000 psi @Temperature 1200 °F |
|
Kennametal Stellite Stellite® 3 PM with P/M Processing Typical applications include (aerospace) vane plugs, fuel metering pins, spacer bushings, (bearings) ball blanks, race blanks, (valve seat inserts) diesel engine exhaust, fluid valve seats, saw cutt.. |
|||
Tensile Strength, Ultimate | 690 MPa @Temperature 649 °C |
100000 psi @Temperature 1200 °F |
|
Kennametal Stellite Stellite® 98M2 with P/M Processing Adhesive wear test data P/M 0.58 Typical applications include vane plugs, fuel metering pins, spacer bushings, ball bearing blanks, race bearing blanks, diesel engine exhaust, fluid valve seats, saw.. |
|||
Tensile Strength, Ultimate | >= 690 MPa | >= 100000 psi | |
MetalTek MTEK 420 Cast UNS J91153 Martensitic Stainless Steel Information provided by MetalTek |
|||
Tensile Strength, Ultimate | >= 690 MPa | >= 100000 psi | |
MetalTek MTEK 6 UNS R30006 Cobalt Base Alloy Non-galling, heat and thermal shock resistance. Heat Resistance.Applications: Bearings and hot work sleeves, housings. Rocket engine partsInformation provided by MetalTek |
|||
Tensile Strength, Ultimate | >= 690 MPa | >= 100000 psi | |
MetalTek MTEK B Cast UNS N24030 Nickel-Copper Alloy Family of alloys for extreme heat and corrosion services.Applications: Gas Turbine parts. Chemical process equipment, heat treating equipment.Information provided by MetalTek |
|||
Tensile Strength, Ultimate | >= 690 MPa | >= 100000 psi | |
MetalTek MTEK SD100 Cast UNS J93380 Duplex Stainless Steel Information provided by MetalTek |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
Haynes Hastelloy® G-30® alloy, mill annealed HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Tensile Strength, Ultimate | 690 - 920 MPa @Diameter 6.35 mm |
100000 - 133000 psi @Diameter 0.250 in |
CWSR; DAN 2700.9 |
Haynes Ti-3Al-2.5V Alloy Titanium Tubing Haynes® Ti-3Al-2.5V alloy is both lightweight and strong, providing a major design advantage - saving weight.Specific alloying additives, notably aluminum, raise the temperature at which a titani.. |
|||
Tensile Strength, Ultimate | 690 MPa @Temperature 538 °C |
100000 psi @Temperature 1000 °F |
|
Haynes Ultimet® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | (Tensile Yield Strength near U.T.S.) |
Kennametal Stellite Stellite® 12 Satisfactory finishing results can be obtained using carbide tipped tools. Applications include cutting plastics, rubber, paper, carpet, and wood; saw teeth, trimmer knives, carpet knives, ledger bl.. |
|||
Tensile Strength, Ultimate | >= 690 MPa | >= 100000 psi | |
MetalTek MTEK 2507 Cast UNS J93404 Duplex Stainless Steel Excellent seawater corrosion resistance combined with nearly twice the strength of common stainless steels.Applications: Offshore piping systems, couplings. Centrifuge, dewatering equipment. Pump, v.. |
|||
Tensile Strength, Ultimate | >= 690 MPa | >= 100000 psi | |
MetalTek MTEK 29M Cast UNS J93370 Duplex Stainless Steel Excellent seawater corrosion resistance combined with nearly twice the strength of common stainless steels.Applications: Offshore piping systems, couplings. Centrifuge, dewatering equipment. Pump, v.. |
|||
Tensile Strength, Ultimate | >= 690 MPa | >= 100000 psi | |
MetalTek MTEK 29MN Cast UNS J93372 Duplex Stainless Steel Information provided by MetalTek |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
Haynes Hastelloy® G-30® alloy, 25.4 mm thick bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
Haynes Hastelloy® G-30® alloy, 9.5 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | Annealed prior to test |
Special Metals BRIGHTRAY® Alloy F Electrical Resistance Alloy A nickel-iron-chromium electrical-resistance alloy for use at temperatures up to 1920°F (1050°C) under continuous operating conditions. Its high iron content and relatively low level of nicke.. |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | Annealed |
Special Metals INCOLOY® Alloy 825 A nickel-iron-chromium alloy with additions of molybdenum and copper. It has excellent resistance to both reducing and oxidizing acids, to stress-corrosion cracking, and to localized attack such as.. |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
CMW® THERMKON® 70M Molybdenum Copper parts For matching CTE of semiconductor substrates while allowing high thermal transfer.Information provided by CMW Inc. |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
ATI Allegheny Ludlum Grade 4 Titanium (UNS R50700) Uses: CPI equipment, industrial components, heat exchangers.Mechanical property data below is typical of annealed samples at room temperature.Information provided by Allegheny Ludlum. |
|||
Tensile Strength, Ultimate | 690 - 800 MPa | 100000 - 116000 psi | |
ArcelorMittal TRIP 690 Very high strength steel, Cold Rolled Steel Available in the following: uncoated (HCT690T), electrogalvanized (HCT690T+ZE) and Extragal®/Galvannealed (HCT690T+Z)Description: TRIP steels offer an outstanding combination of strength and ductil.. |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
ATI Allvac® Nickelvac® H-46 Specialty Steel, Heat Treatment: 1149°C (2100°F) Anneal Data provided by Allvac.Applications: Structural components for land-based turbine engines. Rings and structurals in jet engines. |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
ATI Allvac® Nickelvac® H-X Nickel Superalloy, Heat Treatment: 1177°C (2150°F) Anneal Data provided by Allvac.Applications: Afterburner components, combustion chamber liners, nozzles, vanes, rings, turbine exhaust weldments, structural parts. |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
ATI Allvac® Vasco® 410/403 Specialty Steel, Heat Treatment: 927°C (1700°F) Anneal Data provided by Allvac.Applications: Compressor blades, turbine parts. |
|||
Tensile Strength, Ultimate | >= 690 MPa | >= 100000 psi | |
ATI Allegheny Ludlum AL 276™ Nickel-Base Alloy, UNS N10276 AL 276 alloy is a nickel-chromium-iron-tungsten alloy which is among the most corrosion resistant of alloys currently available. The AL 276 alloy is widely used in the severest environments encount.. |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
ATI Allvac® 3-2.5 Titanium Alloy, Heat Treatment: 704°C (1300°F) Anneal Data provided by Allvac.Applications: Excellent cold formability, 20-50% higher tensile properties than CP titanium grades. Primarily used in aircraft hydraulic systems. |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | |
Haynes Hastelloy® G-30® alloy, 0.71 mm thick sheet HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
Tensile Strength, Ultimate | 690 MPa | 100000 psi | typical |
ATI Allegheny Ludlum AL 825™ Nickel Alloy Allegheny Ludlum AL 825 alloy is an austenitic nickel-iron-chromium-molybdenum-copper alloy containing high levels of corrosion resistance to both moderately oxidizing and moderately reducing enviro.. |