Polymer Property : Tensile Strength, Ultimate = 6.21 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 6.21 MPa
901 psi
Momentive Performance Materials RTV157 Gray Adhesive Sealant, High Strength Paste
One-part cure. Typical uses: High strength adhesive; use for gasketing, aircraft maintenance, and electrical insulation.Data provided by the manufacturer, GE Silicones.GE Silicones became a part of..
Tensile Strength, Ultimate 6.21 MPa
900 psi
Sylvin Technologies 9077-80 LMW Natural PVC for Injection Molding
Information provided by Sylvin Technologies Inc.
Tensile Strength, Ultimate 6.21 MPa
900 psi
Dow Corning SILASTIC® 25787 SILICONE RUBBER NATURAL
Information provided by Dow Corning
Tensile Strength, Ultimate 6.21 MPa
900 psi
Dow Corning SILASTIC® J RTV SILICONE RUBBER BASE & CURING AGENT
High durometer silicone mold making rubber recommended for use with rigid and foam polyurethane and can be used with polyesters and epoxies.Information provided by Dow Corning
Tensile Strength, Ultimate 6.21 MPa
900 psi
ASTM D638
Dow AFFINITY™ EG 8200G Ethylene alpha-olefin copolymer
AFFINITY™ EG 8200G Polyolefin Plastomer (POP) is produced via INSITE™ Technology from Dow Plastics. It exhibits high flexibility and elasticity. It can be utilized in monolayer cast film and in ..
Tensile Strength, Ultimate 6.21 MPa
900 psi
Dow Corning 5-8601 FLUOROSILICONE LSR, KIT
Fluorosilicone rubber designed for liquid injection moldingInformation provided by Dow Corning
Tensile Strength, Ultimate 6.21 MPa
900 psi
Bond strength to metal
Dymax Light Weld® 401 High Clarity Glass Bonding Adhesive
Glass Bonding in SecondsDescriptionDymax Light Weld® 400 Series adhesives form high-clarity, invisible bonds between glass and other substrates in seconds. In addition to many structural glass bond..
Tensile Strength, Ultimate 6.21 MPa
900 psi
silicone property; ASTM D412
Arlon I51576R015 Silicone Rubber/Fiberglass/Alloy Laminate
Top layer of side 2: alloy 600 foil; Bottom layer of side 2: cured silicone rubber; Substrate is 7628 fiberglass; Side 1: cured silicone rubber
Tensile Strength, Ultimate 6.21 - 7.59 MPa
901 - 1100 psi
Arlon Thermavac® 0.020" (0.508 mm) Uncured Silicone Vacuum Bagging (30400R020)
Uncured, unsupported silicone rubber with a thickness of 0.020 in ± 0.002 (0.51 mm ± 0.051) on a Kodacel carrier (0.005 in., 0.13 mm nominal thickness); 0.003 in. (0.08 mm) polyethylene interleave..
Tensile Strength, Ultimate 6.21 MPa
900 psi
silicone property; ASTM D412
Arlon 53423R032 Silicone Rubber/Fiberglass Laminate
Interleave: 3 mil PE; Side 1: cured silicone rubber; Substrate: 2523 fiberglass; Side 2: cured silicone rubber
Tensile Strength, Ultimate 6.21 MPa
900 psi
Dow Corning 3120 RTV SILICONE RUBBER
Two-part, red, condensation cure, moderate flow, high temperature performance, UL HB, cure speed varied by catalyst type and mix ratio.Information provided by Dow Corning
Tensile Strength, Ultimate 6.21 - 37.0 MPa
900 - 5370 psi
Average value: 23.9 MPa Grade Count:23
Overview of materials for Polypropylene Glass Bead Filled
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene Glass Bead Filled". Each property range of values reported is minimum and maximum values o..