Polymer Property : Tensile Strength, Ultimate = 39.3 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	39.3 MPa	5700 psi
Abatron AboCast 8-8/Abocure 8-8 Epoxy (discontinued **) 2-part solvent-free dielectric epoxy casting compound.Processing: 100/50 ratio (pbw); Gel time, 1 lb. (2.2 kg): 135 minutes; cures in 16 hours at 25°C (77°F); postcure: 2 hours at 100°C (212°F)...
Tensile Strength, Ultimate	39.3 - 60.0 MPa	5700 - 8700 psi	Average value: 53.1 MPa Grade Count:3
Overview of materials for Nylon 6/69 This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6/69". Each property range of values reported is minimum and maximum values of appropriate MatWeb ..
Tensile Strength, Ultimate	39.3 MPa	5700 psi	ASTM D638-95
Multibase Multi-ABS 3365 High Impact ABS Data provided by Multibase.
Tensile Strength, Ultimate	39.3 MPa	5700 psi	ASTM D638-95
Multibase Multi-ABS 802 Natural Extrusion Grade Data provided by Multibase.
Tensile Strength, Ultimate	39.3 MPa	5700 psi	ASTM D638
Eastman Tenite Butyrate 264A3720013 Clear, Trsp Cellulose Acetate Butyrate Plasticizer 13%. Weight loss on heating = 0.6% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
Tensile Strength, Ultimate	39.3 MPa	5700 psi
Colorite Polymers 10013G-015 Clear Extrusion Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for the extrusion of various components for the production of devices. The vinyl components used in pre..
Tensile Strength, Ultimate	39.3 MPa	5700 psi
Colorite Polymers 10014G-015 Clear Injection Molding Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for injection molding of various components such as drip chambers, connectors, valves, etc. The vinyl c..
Tensile Strength, Ultimate	39.3 MPa	5700 psi
BCC Products Kwik Kast BC 8001 Urethane Casting BC8001 is an advanced fast cast polyurethane tooling system. It features low viscosity, low exotherm and minimal shrinkage. It cures hard, yet more durable resulting in less brittle parts. Designed..
Tensile Strength, Ultimate	39.3 MPa	5700 psi	ASTM D638
Eastman Tenite Butyrate 465A3720010 Clear, Trsp Cellulose Acetate Butyrate (discontinued **) Plasticizer 10%. Weight loss on heating = 0.9% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..