Polymer Property : Tensile Strength, Ultimate = 30500 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 210 MPa
30500 psi
Same value from ASTM and ISO tests; 5 mm/min.
BASF Capron® 5233G 33% Glass-Filled Nylon 66 (Dry)  (discontinued **)
Capron 5233G is a 33% glass fiber reinforced, polyamide 6,6 injection molding compound offering excellent strength, stiffness, creep resistance and dimensional stability. This balance of engineerin..
Tensile Strength, Ultimate 210 MPa
30500 psi
MarkeTech Aluminum Oxide Ceramic - Alumina 96%
Data provided by the supplier, MarkeTech International.Because of their high temperature, chemical, electrical, and mechanical properties along with their relatively low cost and ease of manufacture..
Tensile Strength, Ultimate 210 MPa
30500 psi
MarkeTech Aluminum Oxide Ceramic - Alumina 97.5%
Data provided by the supplier, MarkeTech International.Because of their high temperature, chemical, electrical, and mechanical properties along with their relatively low cost and ease of manufacture..
Tensile Strength, Ultimate 210 MPa
30500 psi
MarkeTech Aluminum Oxide Ceramic - Alumina 98%
Data provided by the supplier, MarkeTech International.Because of their high temperature, chemical, electrical, and mechanical properties along with their relatively low cost and ease of manufacture..
Tensile Strength, Ultimate 210 MPa
30500 psi
GBC Grade 96 Alumina
Data provided by the manufacturer, GBC Materials Corporation.
Tensile Strength, Ultimate 210 MPa
30500 psi
GBC Grade 97 Alumina
Data provided by the manufacturer, GBC Materials Corporation.
Tensile Strength, Ultimate 210 MPa
30500 psi
GBC Grade 98 Alumina
Data provided by the manufacturer, GBC Materials Corporation.
Tensile Strength, Ultimate >= 210 MPa
>= 30500 psi
MetalTek Bearium® B-11 Bearing Bronze
Exceptional frictional properties as a result of uniformly dispersed microstructure constituents.Applications: Turbine thrust bearings, centrifuge bushings, shaft sleeves, and other severe duty, mis..
Tensile Strength, Ultimate 210 MPa

@Temperature 980 °C
30500 psi

@Temperature 1800 °F
Haynes 556® alloy, hot rolled, solution annealed plate, 6.4-12.7 mm (1/2 in.) thick
Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co..
Tensile Strength, Ultimate 210 MPa
30500 psi
ISO 527
Solvay Technyl® A 218 V35 Nylon 66, 35% Glass Fiber, EH0
Polyamides PA66, reinforced with 35% of glass fiber, heat stabilized, for injection molding.Technyl A 218 V35 is used in all sectors of industry, offering an excellent combination between thermal an..
Tensile Strength, Ultimate 210 MPa
30500 psi
ISO 527
Wellman Wellamid® GF43-66 XE-N 43% Glass Fiber Reinforced Nylon 66, Lubricated & Heat Stabilized
Typical Applications: Radio and TV components, dishwasher roller carriages, chain saw oil reservoirs, gears, housings, door & window latches, power hand tool housings, high temperature devices.Data ..
Tensile Strength, Ultimate 210 MPa
30500 psi
ISO 527-1/-2
DSM Arnite® AV2 390 XT PET GF50
50% Glass Reinforced, Applications with extremely narrow tolerances
Tensile Strength, Ultimate 210 MPa
30500 psi
dry; ISO 527-1/-2
DSM Stanyl® 46HF4530 PA46-GF30
30% Glass Reinforced, Heat Stabilized, High Flow, for E&E applications
Tensile Strength, Ultimate 210 MPa
30500 psi
dry; ISO 527-1/-2
DSM Stanyl® OCD2100 BK27021 PA46-GF40
40% Glass Reinforced, Heat Stabilized
Tensile Strength, Ultimate 210 MPa
30500 psi
dry; ISO 527-1/-2
DSM Stanyl® TW271F8 (PA46+PTFE)-GF40
40% Glass Reinforced, Heat Stabilized, Wear and Friction Modified
Tensile Strength, Ultimate 210 MPa
30500 psi
ISO 527-1/-2
DSM Arnite® AV2 390 XL PET GF50
50% Glass Reinforced, Low outgassing
Tensile Strength, Ultimate 210 MPa
30500 psi
5mm/min; ISO 527
BASF Ultramid® 1503-2 NF2004 33% Glass Filled PA66 (Dry)
Ultramid 1503-2 NF2004 is a 33% glass reinforced, heat stabilized injection molding PA6/6.
Tensile Strength, Ultimate 210 MPa
30500 psi
dry; ISO 527-1/-2
DSM Stanyl® TS200F6 PA46-GF30
30% Glass Reinforced