Polymer Property : Tensile Strength, Ultimate = 305 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 2.10 MPa
305 psi
ASTM D412
Momentive Performance Materials Ultraglaze® 4000 Construction Sealant
High strength, one-part structural glazing/weathersealing system. Cure Method: Alkoxy (Neutral). Tack-free time 2 to 5 hr. Sag/slump 0.1 in.Data provided by the manufacturer, GE Silicones.GE Sili..
Tensile Strength, Ultimate 2.10 MPa
305 psi
ASTM D412
Momentive Performance Materials Ultraglaze® SSG 4000AC Construction Sealant
High strength, one-part, accelerated-cure structural glazing/weathersealing system.Cure Method: Alkoxy (Neutral). Tack-free time 1 hr. Sag/slump 0.1 in.Data provided by the manufacturer, GE Silico..
Tensile Strength, Ultimate 2.10 MPa
305 psi
ASTM D412
Momentive Performance Materials IGS3703 Insulating Glass Sealant
One-component silicone which cures to form a high strength, high modulus sealant with excellent adhesion to glass. Tack-free time 2.5 hr. Peel Strength 50 lb/in. Sag/slump 0.1 in.Data provided by..
Tensile Strength, Ultimate 2.10 MPa
305 psi
ASTM D412
Momentive Performance Materials IGS3713-D1 Insulating Glass Sealant, Black
One-component silicone which cures to form a high strength, high modulus sealant with excellent adhesion to glass. Cure Method: Alkoxy (Neutral). Tack-free time 0.5 hr. Peel Strength 50 lb/in. ..
Tensile Strength, Ultimate 2.10 MPa
305 psi
ASTM D412
Momentive Performance Materials IGS3719-D1 Insulating Glass Sealant, Gray
One-component silicone which cures to form a high strength, high modulus sealant with excellent adhesion to glass. Cure Method: Alkoxy (Neutral). Tack-free time 0.5 hr. Peel Strength 50 lb/in. ..
Tensile Strength, Ultimate 2.10 MPa
305 psi
508 mm/min; ASTM D638
Dow Engage® 8842 Polyolefin Elastomer
Description: Engage® 8842 polyolefin elastomer is an ultra-low density ethylene-octene copolymer with a nominal loose talc surface coating. The talc is untreated and has a nominal 1 µm particle si..