Polymer Property : Tensile Strength, Ultimate = 30.3 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	30.3 MPa	4400 psi	ASTM D638
Multibase Multi-Pro® 2008 X Polypropylene Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase
Tensile Strength, Ultimate	30.3 MPa	4390 psi	ASTM D638-95
Multibase Multi-Pro® 4006 T H BLK 40% Talc Content Polypropylene Multi-Pro 4002 T H is a talc reinforced polypropylene compound with excellent stiffness at medium impact resistance. Its heat resistance is improved over natural and can resist 150°C for 750 hours..
Tensile Strength, Ultimate	30.3 MPa	4390 psi
Indium Corp. IndalloyÂ® 159 Pb-Sn Solder Alloy High temp solder for BGA applications.Information provided by the manufacturer, Indium Corporation.
Tensile Strength, Ultimate	30.3 MPa	4400 psi	0.125 in, injection molded, unannealed; ASTM D638
Styron EMERGEâ„¢ 5710 Acrylonitrile Butadiene Styrene (ABS) EMERGEâ„¢ ABS 5710 advanced resin is an ignition resistant ABS resin with an excellent balance of flow and impact strength. Applications: Monitor Enclosures Surge Protectors and UPS Enclosures ..
Tensile Strength, Ultimate	30.3 MPa	4400 psi
Williams Advanced Alloys WS302 Solder All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys
Tensile Strength, Ultimate	30.3 MPa	4390 psi	ASTM D638
Eastman Tenite Propionate 360E0096916 Natural, Trsp Cellulose Acetate Propionate Plasticizer 16%. Weight loss on heating = 1.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
Tensile Strength, Ultimate	30.3 MPa	4390 psi	ASTM D638
Eastman Tenite Propionate 384A4000016 Clear, Trsp Cellulose Acetate Propionate Plasticizer 16%. Weight loss on heating = 1.3% per ASTM D 707. Soluble matter loss = 0.1% per ASTM D 570.Product Description: TENITE cellulosic plastics are noted for their excellent balance of p..
Tensile Strength, Ultimate	30.3 MPa	4400 psi	ASTM D638
CPC - Vycom POLYCARVE™ Coextruded High Density Sheet (HDPE) PolyCarve™ thermoplastic engraving sign stock made to permanently resist the destructive outdoor elements, and certain indoor environments. PolyCarve is a high density, UV stabilized polyethylene c..
Tensile Strength, Ultimate	30.3 MPa	4400 psi	ASTM D638
CPC - Vycom SANATEC® Sanitary Cutting Boards High Density Polyethylene Sanatec is a high density polyethylene specially formulated for the manufacture of quality cutting boards. Sanatec`s special surface finish insures long product life and will not dull knives. Sanate..
Tensile Strength, Ultimate	30.3 MPa	4400 psi	ASTM D638
CPC - Vycom SEABOARD™ GRIP-X™ Slip Resistant High Density Polyethylene (HDPE) Grip-X is a UV stabilized high density polyethylene (HDPE) sheet formulated to meet demanding conditions of the marine industry. Grip-X is manufactured with a special surface treatment and stipulate..
Tensile Strength, Ultimate	30.3 MPa	4390 psi	ASTM D638
DuPont™ Surlyn® 9720 Ionomer Resin, Zinc Surlyn® 9720 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr..
Tensile Strength, Ultimate	30.3 MPa	4390 psi	ASTM D638
DuPont™ Surlyn® 9721 Ionomer Resin, Zinc Surlyn® 9721 thermoplastic resin is an advanced ethylene/methacrylic acid (E/MAA) copolymer, in which the MAA acid groups have been partially neutralized with zinc ions. The amount of MAA and neutr..
Tensile Strength, Ultimate	30.3 MPa	4400 psi	after optimum cure
Armstrong A-702 Epoxy Adhesive Information provided by Ellsworth Adhesives.
Tensile Strength, Ultimate	30.3 MPa	4400 psi	ASTM D638
BCC Products EB 6200 Epoxy Tooling Board EB6200 is a “grain-free” elevated temperature epoxy modeling material known for its superior surface finish, dimensional stability and the ability to maintain tolerances even after being subjected..
Tensile Strength, Ultimate	>= 30.3 MPa	>= 4400 psi	ASTM D638
Bulk Molding Compounds BMC 940 Vinyl Ester Bipolar Plate Material Bulk Molding Compounds, Inc. is the largest manufacturer of thermoset bulk molding compounds in North America, serving the automotive, appliance, and electrical markets. BMC thermosets are the most ..
Tensile Strength, Ultimate	30.3 MPa @Temperature 871 °C	4390 psi @Temperature 1600 °F
AK Steel 441 Ferritic Stainless steel AK Steel 441 is a 17-18% by weight, chromium and columbium bearing ferritic stainless steel which provides good high-temperature strength (exceeding that of Types 409 and AK Steel 439 LT Stainless S..
Tensile Strength, Ultimate	30.3 - 993 MPa	4400 - 144000 psi	Average value: 206 MPa Grade Count:30
Overview of materials for Vinyl Ester Sheet Molding Compound This property data is a summary of similar materials in the MatWeb database for the category "Vinyl Ester Sheet Molding Compound". Each property range of values reported is minimum and maximum value..
Tensile Strength, Ultimate	30.3 MPa	4390 psi	ASTM Data
Styron Magnum™ 4435 ABS MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM AB..