Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638-95 |
Multibase Multi-Flex® TPO D-6500 Multi-Flex® D 6500 is well suited for TPO extrusion applications and certain high value molded parts for the telecommunications industry.Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
Rotuba MS Cellulose Acetate Property values at 50% RH.Data provided by the manufacturer. |
|||
Tensile Strength, Ultimate | 29.0 - 51.0 MPa | 4210 - 7400 psi | Average value: 39.7 MPa Grade Count:14 |
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded". Each property range of values reported is m.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
North Wood Plastics PS with 40% Wood Fiber Data provided by North Wood Plastics, Inc. |
|||
Tensile Strength, Ultimate | 29.0 MPa @Temperature 90.0 °C |
4210 psi @Temperature 194 °F |
ISO 527 |
LATI LATILUB 73/13-01M Polyoxymethylene Base (POM), 1% Molybdenum Disulfide Self Lubricating Plastic
(Unv Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intri.. |
|||
Tensile Strength, Ultimate | 29.0 MPa @Temperature 60.0 °C |
4210 psi @Temperature 140 °F |
ISO 527 |
LATI LATILUB 73/13-20T Polyoxymethylene Base (POM), 10% Mixed PTFE Self Lubricating Plastic
(Unverified D Description: Latilub self-lubricating plastic materials are more and more often designed to replace metals in applications such as gears, bushings, cams, slides, etc), for which, besides their intri.. |
|||
Tensile Strength, Ultimate | 29.0 - 40.0 MPa | 4210 - 5800 psi | Average value: 34.4 MPa Grade Count:16 |
Overview of materials for High Density Polyethylene (HDPE), Film Grade This property data is a summary of similar materials in the MatWeb database for the category "High Density Polyethylene (HDPE), Film Grade". Each property range of values reported is minimum and max.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | Vulcanized |
KKPC KOSYN 1500NF Styrene Butadiene Rubber Styrene Butadiene RubberCharacteristics: KOSYN SBR, a useful synthetic rubber, is a copolymer made from butadiene and styrene by cold emulsion polymerization. It has superior abrasion resistance and.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM Data |
Styron Magnum™ 9043 ABS, High Gloss Sheet Extrusion Grade MAGNUM® ABS resins are thermoplastic materials which provide an excellent balance of processability, impact resistance and heat resistance as imparted by the various polymer compositions. MAGNUM .. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4200 psi | |
Williams Advanced Alloys WS295 Solder All Williams alloys are available in a variety of shapes and forms, including ribbon, preforms, rod, ring, wire, and custom shapes.Information provided by Williams Advanced Alloys |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
Total PPR 7525MZ Polypropylene, Injection Molding Grade Clarified random copolymer for injection moldingClarity - FINA 7525MZ exhibits superior clarity in molded parts.Impact - FINA 7525MZ produces molded parts with improved impact compared with parts mo.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ISO 37 |
Lubrizol ESTANE® 58280 Ether Based Thermoplastic Polyurethane (European Grade) Description: Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability .. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4200 psi | ASTM D638 |
American Polymers API 505 Polystyrene API 505 is an intermediate grade of impact modified polystyrene. This material has exceptional moldability and colorability.Applications: API 505 is widely used in housewares, toys, containers, dis.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
Eastman PROVISTA Copolymer PETG Copolyester Color, b* CIELAB, Illuminant D6500, 10° Observer is 0.61 per ASTM D 2244.Product Description: PROVISTA Copolymer is a resin specifically developed for extrusion into profiles where aesthetics like.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638/D412 |
Covestro Bayflex® XGT-140 Polyurethane Elastomeric RIM, MDI-based 2-Component Liquid System 0.125 in. thickness. RIM = Reaction Injection MoldingInformation provided by Bayer Corporation, Polyurethanes DivisionAs of 1 September 2015, Bayer MaterialScience was separated from Bayer AG and of.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ISO 527 |
DSM Fibre Intermediates Nyrim® 3000 (Conditioned) Conditioned at 23°C and 50% Relative Humidity.Nyrim is a Block Copolymer of Nylon 6 and an elastomer with exceptional properties in impact resistance, fatigue and abrasion resistance. Nyrim is proc.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | Die C (35 min / 145°C); ASTM D412 |
Dow Buna® SB 1502 Cold polymerized Emulsion Styrene Butadiene Rubber (E-SBR) Buna® SB 1502 - Schkopau is manufactured by cold polymerization using mixed rosin acid / fatty acid soaps. A non-discoloring stabilizer is added during the production process. Buna® SB 1502 - Sc.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM Data |
Dow Retain® PS-4578 Polystyrene Data provided by Dow Chemical. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
Adell EZ-14 Homopolymer Polypropylene, 20% Calcium Carbonate Filled Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4200 psi | after optimum cure |
Armstrong A-5/E Epoxy Adhesive Information provided by Ellsworth Adhesives. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
A. Schulman ComAlloy Comshield® 104 Homopolymer Polypropylene, Electrically Conductive - Carbon Black Filled Data provided by the manufacturer, ComAlloy International Company.The ComAlloy product line has been integrated into the A Schulman product line. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
Buckeye Polymers BP RPP 3019 TU Polypropylene, 30% Mineral Filled UV StabilizedThis Talc-filled product exhibits excellent properties such as high stiffness, surface aesthetics, low coefficient of thermal expansion, low shrinkage, improved scratch and mar resistan.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM D638 |
Devcon Wear Guard (High Load) Epoxy Abrasion-Resistant SystemComments: PuttyData provided by Ellsworth Adhesives. |
|||
Tensile Strength, Ultimate | 29.0 - 75.0 MPa | 4210 - 10900 psi | Average value: 58.4 MPa Grade Count:31 |
Overview of materials for Acrylic, Extruded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Extruded". Each property range of values reported is minimum and maximum values of appropriate .. |
|||
Tensile Strength, Ultimate | 29.0 - 80.0 MPa @Temperature -40.0 - 120 °C |
4210 - 11600 psi @Temperature -40.0 - 248 °F |
Average value: 45.0 MPa Grade Count:4 |
Overview of materials for Nylon 6, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Nylon 6, Unreinforced". Each property range of values reported is minimum and maximum values of appropri.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ASTM Data |
Americas Styrenics Styron® 425 High Impact Polystyrene
(discontinued **) STYRON® 425 impact polystyrene resin is typically used in thin section parts, hot drink cups and cassettes. It offers heat resistance, easy flow, fast cycling, and excellent tensile and flex proper.. |
|||
Tensile Strength, Ultimate | 29.0 MPa | 4210 psi | ISO 37 |
Lubrizol ESTANE® 58238 Ester Based Thermoplastic Polyurethane (European Grade) Estane® thermoplastic polyurethanes (TPUs) include elastomeric materials that bridge the gap between flexible rubber and rigid plastics. These materials offer toughness and durability in a flexible.. |
|||
Tensile Strength, Ultimate | 29.0 - 39.0 MPa | 4210 - 5660 psi | ISO 527 |
BASF Ecovio® C2203 F Blend Biodegradable Polyester Description: Ecovio® F Blend C2203 is our biodegradable film product containing renewable resources. It is basically a compound of our biodegradable copolyester Ecoflex® F Blend and polylactic aci.. |
|||
Tensile Strength, Ultimate | 29.0 - 153 MPa | 4210 - 22200 psi | Average value: 101 MPa Grade Count:42 |
Overview of materials for Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified This property data is a summary of similar materials in the MatWeb database for the category "Polybutylene Terephthalate (PBT), Glass Filled, Impact Modified". Each property range of values reported.. |