Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 19.3 - 28.3 MPa | 2800 - 4100 psi | ASTM D638-95 |
Multibase Multi-Flex® TPO D 5302 E BLK Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D638-95 |
Multibase Multi-Flex® TPO D-6510 Data provided by Multibase. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D638 |
Multibase Multi-Pro® 2502 C Natural Polypropylene Forms:PelletsProcessing Methods:Injection MoldingInformation provided by Multibase |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D412-80 |
DuPont Performance Polymers Hypalon® 48 Chlorosulfonated Polyethylene Rubber, Peroxide Cured Carbon Black Filled Compound Carbon black compound with 100 parts Hypalon; 40 parts carbon black; 20 parts magnesia; and 5.8 parts Varox® DBPH-50. Physical property data below (except mooney viscosity) are for vulcanizate. Ma.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D638 |
Multibase Multi-Pro® 5002 CU Natural Polypropylene Forms:PelletsProcessing Methods:Injection MoldingFeatures:Gloss, LowInformation provided by Multibase |
|||
Tensile Strength, Ultimate | 19.3 - 85.0 MPa | 2800 - 12300 psi | Average value: 64.0 MPa Grade Count:200 |
Overview of materials for Acrylic, General Purpose, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, General Purpose, Molded". Each property range of values reported is minimum and maximum values .. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | |
Sylvin Technologies 8925-95 Natural PVC Extrusion Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | |
Sylvin Technologies 9915-95 Natural PVC Molding Compound Information provided by Sylvin Technologies Inc. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM Data |
Dow AIM® 4800 High Impact Styrenic Resin AIM® 4800 advanced styrenic resin is designed to offer the processability of high impact polystyrene and the gloss and practical toughness of high gloss ABS. It can be processed at lower temperatur.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM Data |
Dow AIM® 4810 High Impact Styrenic Resin AIM® 4810 advanced styrenic resin is designed to offer the processability of high impact polystyrene and the gloss and practical toughness of high gloss ABS. It can be processed at lower temperatur.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D638 |
Colorite Polymers 9614 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D412 |
Colorite Polymers CS6023GP Wire and Cable Insulation Vinyl Compound Description: Colorite specialty wire and cable compounds feature low smoke properties, excellent flame retardance, low temperature flexibility, and resistance to abrasion and chemicals. All are avai.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | |
Colorite Polymers Self Frosting™ 8511SF Vinyl Compound Description: Colorite has developed a family of vinyl compounds to satisfy the needs of those who need a smooth, low gloss, low friction surface for the products that they produce. Historically, thi.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D638 |
Dow AMPLIFY™ VA 400 Ethylene vinyl acetate (EVA) AMPLIFY™ VA 400 Functional Polymer is produced via a high pressure reactor. It exhibits high flexibility, clarity and low temperature sealability. It is easy to process and features functional .. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D638 |
Colorite Polymers 8200FR General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | |
Colorite Polymers 8511 Clear Extrusion Vinyl Compound Description: Clear non-toxic vinyl compounds are utilized by the health and medical industries for the extrusion of various components for the production of devices. The vinyl components used in pre.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D638 |
Colorite Polymers 8588 Non-Phthalate 88 Series Vinyl Compound Description: The Colorite 88 series is a family of vinyl non-toxic compounds formulated to provide excellent low temperature flexibility characteristics. These compounds are designed for outside doo.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D638 |
Colorite Polymers 9033 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D638 |
Colorite Polymers 9034 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D638 |
Colorite Polymers 9204 General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D412 |
Colorite Polymers CS9038UL Wire and Cable Insulation Vinyl Compound Description: Colorite specialty wire and cable compounds feature low smoke properties, excellent flame retardance, low temperature flexibility, and resistance to abrasion and chemicals. All are avai.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | Cured property; ASTM D412 |
Aptek 2503R-A/B Premeasured conformal urethane coating repair kit APTEK 2503-A/B is an unfilled, two component, electrically insulating, transparent, flexible urethane coating system designed for the encapsulation and protection of electrical/electronic components.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D638 |
Arkema Group Solarkote® P-611 Acrylic PVC capstock, white, low glossInformation provided by Arkema Group |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | 2 in/min (50 mm/min); ASTM D638 |
Bapolene® 4082 Polypropylene, Injection Grade Bapolene PP4082 is a high flow, fast cycle injection molding resin. Injection molded parts exhibit good stiffness and chemical resistance. This product meets FDA standards for food contact applica.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | Cured property; ASTM D412 |
Aptek 2503-A/B Low modulus urethane conformal coating APTEK 2503-A/B is an unfilled, two component, electrically insulating, transparent, flexible urethane coating system designed for the encapsulation and protection of electronic services mounted on p.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D638 |
Colorite Polymers 8007SF General Purpose Vinyl Compound Description: Colorite produces many vinyl compounds. They have the compounds that perfectly suit whatever the application. Requirements such as ultraviolet ray resistance, fungus resistance, flame r.. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D638 |
Adell RZ-18 Copolymer Polypropylene, 40% Calcium Carbonate Filled Data provided by Adell Plastics, Inc. |
|||
Tensile Strength, Ultimate | 19.3 MPa | 2800 psi | ASTM D412; ASTM D638 |
Lubrizol Estane® 58252 Thermoplastic Polyurethane Type: Estane® 58252 is a 70A polyether-type thermoplastic polyurethane (TPU).Features: Formulated to have one of the highest MVT values within the thermoplastic polyurethane class. It is also amon.. |
|||
Tensile Strength, Ultimate | >= 19.3 MPa | >= 2800 psi | |
Technetics Group PLASTOLON™ Skived PTFE Tape
(Unverified Data**) Information provided by Technetics Group (formerly Plastomer Technologies) |
|||
Tensile Strength, Ultimate | 19.3 - 117 MPa | 2800 - 17000 psi | Average value: 45.5 MPa Grade Count:20 |
Overview of materials for Polypropylene, Carbon Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene, Carbon Fiber 10%". Each property range of values reported is minimum and maximum values o.. |