Polymer Property : Tensile Strength, Ultimate = 26.5 MPa Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 26.5 - 45.0 MPa
3840 - 6530 psi
Average value: 35.7 MPa Grade Count:63
Overview of materials for Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant". Each property range of values rep..
Tensile Strength, Ultimate 26.5 - 41.4 MPa
3840 - 6000 psi
Average value: 35.1 MPa Grade Count:4
Overview of materials for ABS/Polyester Alloy
This property data is a summary of similar materials in the MatWeb database for the category "ABS/Polyester Alloy". Each property range of values reported is minimum and maximum values of appropriat..
Tensile Strength, Ultimate 26.5 MPa
3840 psi
ASTM D638
KKPC Kuhmo HF 402 Flame Retarded General Purpose HIPS
Key features: Good mechanical balance, High Strength. Common Uses: Parts needing strength.HIPS is a functional resin made by copolymerization of styrene monomer and PBR. It shows excellent balance b..
Tensile Strength, Ultimate 26.5 MPa
3840 psi
150°C, 40 min., Pressure Vulcanization. -1% Change after 100°C, 70 hrs, Oil Immersion
KKPC KOSYN KNB 40M Acrylonitrile Butadiene Rubber (NBR)
Acrylonitrile Butadiene Rubber (NBR)Characteristics: KOSYN KNB is copolymer of high oil resistance and chemical resistance made from acrylonitrile and butadiene by the cold emulsion polymerization. ..
Tensile Strength, Ultimate 26.5 MPa
3840 psi
ASTM D638
KKPC Kuhmo HI 425TVD High Flow/High Heat Resistant HIPS
Key features: High-impact-fluidity. Common Uses: TV cover, computer case.HIPS is a functional resin made by copolymerization of styrene monomer and PBR. It shows excellent balance between impact-res..
Tensile Strength, Ultimate 26.5 MPa
3840 psi
ASTM D638
SK Chemicals SKYPEL G140D General Grade
SKYPEL is a thermoplastic polyester elastomer (TPEE). It is a polymer resin having the property somewhere between plastics and rubber, which have various properties ranging from high hardness plasti..
Tensile Strength, Ultimate 26.5 MPa
3840 psi
ASTM D638
Samyang Triel® 5552EM Thermoplastics Polyetherester Elastomer, Extrusion
Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5552EM is an extrusion grade.Information provided by Samyang.
Tensile Strength, Ultimate 26.5 MPa

@Temperature 260 °C
3840 psi

@Temperature 500 °F
ASTM D1708
Daelim H&L Plavis-G40 DF 40% Graphite Filled Aromatic Polyimide Bearing
Direct Formed. Plavis-G-40: Graphite 40 wt% filled, Self lubricating grade with low thermal expansion.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 carbons is..
Tensile Strength, Ultimate 26.5 MPa
3850 psi
after optimum cure
Armstrong C-7/W Epoxy Adhesive, 2:3 Mix Ratio
A clear, unfilled, medium viscosity adhesive recommended for use with any Armstrong Activator. Physical property data included covers C-7 used with Activators W and H-20. All other Activators may ..
Tensile Strength, Ultimate 26.5 MPa
3850 psi
after optimum cure
Armstrong X-81/A Epoxy Adhesive
Information provided by Ellsworth Adhesives.
Tensile Strength, Ultimate 26.5 MPa
3840 psi
ASTM D638
Samyang Triel® 5550 Thermoplastics Polyetherester Elastomer, General Extrusion
Excellent mechanical characteristics, elasticity, thermal resistance and chemical resistance.5550 is an extrusion grade.Information provided by Samyang.